| 牌号简介 About |
|---|
| Polytrope Str 1032eu树脂是一种经济高效、高熔融强度的热塑性TPO材料，其抗冲击性和刚度与ABS相似，但具有尺寸稳定性、耐化学性和耐候性等优点。它可以在光滑或纹理表面挤压，或与增强聚烯烃帽树脂共同挤压，以进一步定制其耐用性，外观，或内部和外部应用的感觉。Polytrope Str 1032eu在挤压和热成型过程中提供非常光滑的表面的能力使其非常适合用装饰膜层压工艺。它也很容易上色，可通过标准TPO油漆系统进行喷漆。 POLYTROPE STR 1032EU resin is a cost efficient, high melt strength thermoformable TPO material that provides an economical balance of impact resistance and stiffness similiar to ABS, but provides the benefits of dimensional stability, chemical and weathering resistance characteristic of TPO materials. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 1032EU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems. |
产品描述 Product Description
加工条件：热成型,共挤出成型,片材挤出成型,型材挤出成型 Thermo forming,Extrusion,Profile extrusion
性能特点： 可回收; 熔体强度好; 防火阻燃等级HB; 可表面喷涂; 热膨胀系数低; 韧性好; 耐候抗UV; Good melt strength,Sprayable,Good flexibility,Low CLTE,HB,Renewable resources,Weather resistance is good
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.13 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
0.70 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
23℃，3.2 mm，24 hrs 23℃，3.2 mm，24 hrs |
0.80 to 1.2 | % | ISO 294-4 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
23.0 | MPa | ISO 527-2 |
|
拉伸应变 Tensile strain |
|||
|
断裂，233℃ Fracture, 233 ℃ |
430 | % | ISO 527-2 |
|
弯曲模量 Bending modulus |
|||
|
弦，23℃ String, 23 ℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
流量，-30℃，3.2mm，注塑成型 Flow rate, -30 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
|
流量，23℃，3.2mm，注塑成型 Flow rate, 23 ℃, 3.2mm, injection molding |
ASTM D256 | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
0℃，Total Energy，Ductile Failure 0℃，Total Energy，Ductile Failure |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-30~100℃ MD：-30~100℃ |
1/℃ | ASTM E831 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60°，3180 µm，热塑，光滑 60 °, 3180 µ m, thermoplastic, smooth |
ISO 2813 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Heat Sag（8 inch span，two point support，149℃，3.20 mm） Heat Sag（8 inch span，two point support，149℃，3.20 mm） |
mm | ASTM D3769 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 方法 A |
| 3 类型 1, 2.0 in/min |
| 4 类型1A, 0.079 in/min |
|
【新闻资讯】查看全部 
立即关店！星巴克中国回应门店饮品原料过期问题
2021-12-14 搜料网资讯： 位于上海的星巴克企业管理（中国）有限公司13日下午回应了当天有媒体报道的无锡市两家星巴克门店存在的饮品原料过期、篡改已标注的食材使用限定日期等问题。星巴 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付