牌号简介 About |
---|
伊斯曼Tritan™ VX351HF是一种无定形共聚酯,具有优异的透明度和抗冲击性。优异的耐化学性、水解稳定性和易加工性使Tritan™ VX351HF成为广泛光学应用的理想选择,如太阳镜镜片、光学玻璃镜片和安全眼镜。 Eastman Tritan™ VX351HF is an amorphous copolyester with excellent clarity and impact resistance. The outstanding chemical resistance, hydrolytic stability, and ease of processing make Tritan™ VX351HF an ideal candidate for a broad spectrum of optical applications such sunglass lenses, optical glass lenses and safety eyewear. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃ -40℃ |
110 | J/m | ASTM D256 |
23℃ 23℃ |
860 | J/m | ASTM D256 |
-40℃ -40℃ |
11 | kJ/m² | ISO 180 |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-40℃ -40℃ |
|||
23℃ 23℃ |
|||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
-40℃,Energy at Peak Load -40℃,Energy at Peak Load |
J | ||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM C1648 | ||
透光率 Transmittance |
|||
总计 total |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
色散系数 Dispersion coefficient |
|||
127.0 µm 127.0 µm |
ASTM C1648 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
2021中国乙烯量缺口近1500万吨
2017-05-11 在新一轮以民营化企为主掀起的乙烷裂解项目投资热潮的当儿,企业也因利润等驱动而大举布局实施煤化工和石化烯烃项目。亚化咨询预计,到2021年,中国乙烯产能将达到3700万吨,当量需求将达到4400万吨左右,当量缺口约为1500万吨,届时中国乙烯市场依然存在巨大缺口。随着拟在建项目的落成,继煤/甲醇制烯烃之后,中国的乙烯市场格局迎来了又一场巨震。 近年,在大量煤/甲醇制烯烃,丙烷脱氢制丙烯,混烷脱氢项目投产的背景下,中国丙烯产能增速明显超过乙烯,而中国乙烯需求量及供需缺口远大于丙 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |