牌号简介 About |
---|
杜邦Vamac® GLS是乙烯、丙烯酸甲酯的三元共聚物,以及使用二胺基硫化系统固化的固化部位单体。与Vamac G相比,Vamac® GLS可显著提高对机油膨胀和柴油等化学品的抵抗力。Vamac® GLS弹性体含有少量加工助剂,标称比重为1.06。它有轻微的丙烯酸气味。储存稳定性极佳。 DuPont™ Vamac® GLS is a terpolymer of ethylene, methyl acrylate, and a cure site monomer cured using a diamine-based vulcanization system. Compared with Vamac® G, Vamac® GLS offers significantly improved resistance to oil swell and chemicals such as diesel fuel. Vamac® GLS elastomer contains a small amount of processing aid and has a nominal specific gravity of 1.06. It has a mild acrylic odor. Storage stability is excellent. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
门尼粘度 Mooney viscosity |
ASTM D1646 | ||
ML 1+4,100℃ ML 1+4,100℃ |
19 | MU | |
MS 1,121℃ MS 1,121℃ |
> 15 | MU | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
68 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
16.1 | MPa | ASTM D412 |
100% 应变 100% strain |
6.40 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 1 |
|||
23℃ 23℃ 1 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395 | ||
150℃,70 hr 150℃,70 hr |
% | ||
150℃,168 hr 150℃,168 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
150℃,168 hr 150℃,168 hr |
% | ||
100% 应变,150℃,168 hr 100% strain, 150 ℃, 168 hr |
% | ||
175℃,336 hr 175℃,336 hr |
% | ||
100% 应变,175℃,336 hr 100% strain, 175 ℃, 336 hr |
% | ||
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
150℃,168 hr 150℃,168 hr |
% | ||
175℃,336 hr 175℃,336 hr |
% | ||
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
支撐 A,150℃,168 hr Support A, 150 ℃, 168 hr |
|||
支撐 A,175℃,336 hr Support A, 175 ℃, 336 hr |
|||
体积变化 Volume change |
|||
150℃,70 hr,在IRM 903油中 150 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Mooney Scorch(Time to 10unit rise,121℃) Mooney Scorch(Time to 10unit rise,121℃) |
min | ASTM D1646 | |
挥发性 volatility |
wt% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
郑州塑博会砥砺奋进的五年
2017-10-23 近期,正值全国第十九届党代会召开之际。总结过去,展望未来已成为各行业人士所关注的热门词汇。对于SINO-PLAS中国郑州塑料产业博览会来说,如果以五年为一个节点,那么过去的五年可谓是砥砺奋进的五年。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |