牌号简介 About |
---|
SABIC® LDPE 2501N0W是一种无添加剂的具有低凝胶水平的级,它结合了良好的拉伸能力和良好的光学性能和刚度。应用SABIC® LDPE 2501N0W通常用于尿布膜、表面保护膜、层压膜,以及需要低阻塞性能且不需要存在滑动和防阻塞的应用。由于迁移水平非常低,SABIC® LDPE 2501N0W通常可用于食品应用。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LDPE 2501N0W is a grade without additives with a low gel level, which combines good draw down ability with fair optical properties and stiffness. Application SABIC® LDPE 2501N0W is typically used in diaper film, surface protection film, lamination film and in applications where low blocking behaviour is required and the presence of slip and anti block is unwanted. SABIC® LDPE 2501N0W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.75 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
0.90 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
弹性模量 Elastic modulus |
|||
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
200 | MPa | ASTM D882 |
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ||
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁冲击强度 Izod notched impact strength |
|||
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻塞力 Blocking force |
|||
吹塑薄膜,50.0 µm Blow molded film, 50.0 µ m |
g | 内部方法 | |
Re-blocking - 吹塑薄膜(50.0 µm) Re blocking - blow molded film (50.0 µ m) |
g | 内部方法 | |
撕裂强度 tear strength 1 |
ISO 6383-2 | ||
MD,50 µm MD,50 µm |
kN/m | ||
TD,50 µm TD,50 µm |
kN/m | ||
memo_intro memo_intro |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部
中国五环携手巴斯夫等研发天然气CO2制合成气技术,助力“双碳”
2022-01-14 搜料网资讯: 近日,中国五环与行业领先的天然气开发加工企业中海石油化学股份有限公司及世界著名化工企业、催化剂行业领头羊企业巴斯夫在北京签署了联合开发协议。三方将共同 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |