Jampilen RP340N是一种聚丙烯无规共聚物,具有极高的流动性、良好的透明度、高光泽和良好的抗静电性能。Jampilen RP340N主要用于透明家居用品和高质量包装应用。对于注模容器和薄壁包装来说,它是一个优秀的等级,在这些包装中,清晰度是最重要的。在这些应用中,Jampilen RP340N可以取代PS,因为它可以匹配光学性能,同时增加低重量,低气味转移,耐化学性和冲击强度。 "Jampilen RP340N" is a polypropylene random copolymer which features extremely high flow properties, excellent transparency, high gloss and exhibits good antistatic properties. "Jampilen RP340N" is mainly designed for transparent housewares and quality packaging applications. It is an outstanding grade for injection molded containers and thin-walled packaging where clarity is ofutmost importance. In many of these applications, "Jampile RP340N" can replace PS since it can match the optical properties whilst adding low weight, low odor transfer, chemical resistance and impact strength. Features: High flow properties Excellent transparency High gloss Good antistatic properties Random copolymer Typical Applications: Injection molded containers and thin-walled packaging Clear containers Household articles Packaging for food, cosmetics and pharmaceutical products Lids, caps and closures Coextrusion with other polypropylene resins to produce multilayer sheet for thermoforming trays for fresh pasta and bakery products Sports, Leisure and toys |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
11 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
85 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
83.0 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
128 | ℃ | ASTM D1525 2 |
加速干燥箱老化 Accelerate oven aging |
|||
150℃ 150℃ |
hr | ASTM D3012 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60° 60° |
ASTM D2457 | ||
雾度 Haze |
|||
1000 µm 1000 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
如何从塑料制品的设计上预防应力开裂?
2018-02-27 如何从塑料制品的设计上预防应力开裂?有以下几点。 塑料制品的形状和尺寸 在具体设计塑料制品时,为了有效地分散内应力,应遵循这样的原则:制品外形应尽可能保持连续性,避免锐角、直角、缺口及突然扩大或缩小。 对于塑料制品的边缘处应设计成圆角,其中内圆角半径应大于相邻两壁中薄者厚度的70%以上;外圆角半径则根据制品形状而确定。 对于壁厚相差较大的部位,因冷却速度不同,易产生冷却内应力及取向内应力。因此 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |