| 牌号简介 About |
|---|
| GM5010T2U是一种高摩尔质量的高密度聚乙烯化合物，专门为脐带电缆护套的制造而开发。采用双峰工艺生产，力学性能高，抗应力开裂性能优异。GM5010T2U含有炭黑颜料，可防止紫外线辐射和光降解。用途：用于油田平台的脐带管、立管和采气管线的护套。工艺：挤压。 GM5010T2U is a High Density Polyethylene compound with high molar mass specially developed for the manufacturing of jacketing of umbilicals. It is produced with bimodal technology, shows high mechanical properties and has excellent resistance to stress cracking. GM5010T2U contains carbon black pigment that protects it against ultraviolet radiation action and photodegradation. Application: Jacketing of umbilicals, risers and flowlines for oil field platforms. Process: Extrusion. |
产品描述 Product Description
加工条件：挤出 Extrusion
性能特点： 高密度; 高分子量; 抗应力开裂; High molecular weight,High density,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.955 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，5.0kg 190℃，5.0kg |
0.45 | g/10min | ASTM D1238 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
2.00 mm，100%非离子表面活性剂，模压成型，F50 2.00 mm, 100% non-ionic surfactant, molded, F50 |
> 1000 | hr | ASTM D1693 |
|
炭黑含量 Carbon black content |
2.3 到 2.7 | % | ASTM D1603 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
模压成型 Compression Molding |
220 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火，模压成型 0.45 MPa, unannealed, molded |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 1 | |
|
氧感应时间 Oxygen sensing time |
|||
|
220℃ 220℃ |
min | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，模压成型 Shaw's D, molded |
ASTM D2240 | ||
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
屈服，模压成型 Yield, molding |
MPa | ||
|
断裂，模压成型 Fracture, molded |
MPa | ||
|
拉伸应变 Tensile strain |
ASTM D638 | ||
|
屈服，模压成型 Yield, molding |
% | ||
|
断裂，模压成型 Fracture, molded |
% | ||
|
弯曲模量 Bending modulus |
|||
|
1% 正割，模压成型 1% cut, molded |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部 
中韩石化乙烯出厂创新高
2021-12-21 搜料网资讯： 今年前11个月，中韩石化完成乙烯出厂2933车次 ，累计装车6.7万吨，是去年全年装车量的2.85倍，创乙烯出厂最高纪录。 中韩石化烯烃部乙烯装置在去年底的大检修中，产能 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付