牌号简介 About |
---|
Adflex Q 100 F是一种热塑性聚烯烃,主要用于吹塑薄膜的挤出。也适用于板材挤压。Adflex Q 100 F具有很高的柔软度和很低的模量。它不包含任何滑动或防阻塞剂。Adflex Q 100 F用于生产柔软的卫生薄膜和重型薄膜,以及对低密度聚乙烯(LDPE)或低密度聚乙烯(LLDPE)进行改性,以增加机械特性、抗穿刺性,并允许进一步下量。它可以很容易地在传统的低密度聚乙烯或低密度聚乙烯吹塑薄膜生产线上加工。 Adflex Q 100 F is a thermoplastic polyolefin, which is mainly used by our customers for the extrusion of blown film. It is also suitable for sheet extrusion. Adflex Q 100 F features very high softness and very low modulus. It does not contain any slip or anti-blocking agents. Adflex Q 100 F is used for the production of soft hygienic film and heavy duty film, as well as for the modification of LDPE or LLDPE to increase mechanical characteristics, puncture resistance, and to allow further downgauging. It can be easily processed on conventional LDPE or LLDPE blown film lines. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.880 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.60 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
30 | ISO 868 | |
弯曲模量 Bending modulus |
100 | MPa | ISO 178 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-3/25 | ||
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
90.0 | MPa | ISO 527-3/25 |
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ISO 527-3/25 | |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
断裂 fracture |
MPa | ISO 527-2 | |
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3/500 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
断裂 fracture |
% | ISO 527-2 | |
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
% | ISO 527-3/500 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
% | ISO 527-3/500 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃ -20℃ |
ISO 180/1A | ||
23℃ 23℃ |
ISO 180/1A | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50 µm 45°,50 µm |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
原油大幅收涨终结七连跌 并创三月以来最大单日百分比涨幅
2021-08-24 搜料网资讯: 8月24日消息,原油期货价格周一大幅上扬,创三月以来最大单日百分比涨幅。此前因人们担心导致新型冠状德尔塔变种病毒的继续传播将削弱原油需求,原油价格上周创三 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |