| 牌号简介 About |
|---|
| NANCAR® 1032是一种中高丙烯腈-丁二烯共聚物，具有良好的耐油性。它在低温下聚合，并含有足够的抗氧化剂，以满足正常老化条件。它具有很高的耐水性，对金属无腐蚀性。NANCAR® 1032是一种优良的多用途丁腈橡胶。特别推荐用于具有低金属腐蚀性和高耐水性的耐油橡胶零件。 NANCAR® 1032 is a medium high acrylonitrile butadiene copolymer with good oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It is highly water resistant, and non-corrosive to metal. NANCAR® 1032 is an excellent multi-purpose nitrile rubber. It is particularly recommended for use in oil resistant rubber parts with low metal corrosion and high water resistance. |
产品描述 Product Description
用途：管道;通用;密封件;传送带修补;橡胶取代;垫圈;
性能特点： 无腐蚀性; 耐磨; 耐油; 共聚物; 抗氧化; Non-corrosiveness,Inoxidizability,Copolymer,Good wear resistance,Grease resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.00 | g/cm³ | |
|
门尼粘度 Mooney viscosity |
|||
|
ML 1+4，100℃ ML 1+4，100℃ |
63 | MU | ASTM D1646 |
|
丙烯腈含量（Bound） Acrylonitrile content (Bound) |
33.0 | % | 内部方法 |
|
Stabilizer Stabilizer |
Non-staining | ||
|
可溶性 solubility |
|||
|
in MEK in MEK |
100 | % | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A Shaw's A 2 |
ASTM D2240 | ||
|
邵氏 A Shaw's A 3 |
ASTM D2240 | ||
|
邵氏 A Shaw's A 4 |
ASTM D2240 | ||
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 6 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 7 |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
屈服 yield 2 |
MPa | ASTM D412 | |
|
屈服 yield 3 |
MPa | ASTM D412 | |
|
屈服 yield 4 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂 fracture 5 |
% | ASTM D412 | |
|
断裂 fracture 6 |
% | ASTM D412 | |
|
断裂 fracture 7 |
% | ASTM D412 | |
|
撕裂强度 tear strength 8 , 3 |
kN/m | ASTM D624 | |
|
压缩形变 Compression deformation 4 |
|||
|
100℃，70 hr 100℃，70 hr 4 |
% | ASTM D395 | |
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
空气中拉伸强度的变化率 The rate of change in tensile strength in air 3 |
|||
|
100℃，70 hr 100℃，70 hr 3 |
% | ASTM D865 | |
|
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 3 |
|||
|
100℃，70 hr 100℃，70 hr 3 |
% | ASTM D865 | |
|
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 3 |
|||
|
邵氏 A，100℃，70 hr Shore A, 100 ℃, 70 hr 3 |
ASTM D865 | ||
|
拉伸强度的变化率 The rate of change in tensile strength 3 |
ASTM D471 | ||
|
100℃，在水中 100 ℃ in water |
% | ASTM D471 | |
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
|
极限伸长率的变化率 Change rate of ultimate elongation 3 |
ASTM D471 | ||
|
100℃，在水中 100 ℃ in water |
% | ASTM D471 | |
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
|
邵氏硬度的变化率 The rate of change in Shore hardness 3 |
ASTM D471 | ||
|
100℃，在水中 100 ℃ in water |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在ASTM #3油中 Support A, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
|
体积变化 Volume change 3 |
ASTM D471 | ||
|
100℃，在水中 100 ℃ in water |
% | ASTM D471 | |
|
100℃，70 hr，ASTM 标准油（1号） 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
|
100℃，70 hr，ASTM 标准油（3号） 100 ℃, 70 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热损耗 Heat loss |
% | ASTM D5688 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Corrosion（Rating） Corrosion（Rating） |
|||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 硫化 20,0 min 在 302°F |
| 3 硫化 40,0 min 在 302°F |
| 4 硫化 60,0 min 在 302°F |
| 5 Cured for 60.0 min at 150°C |
| 6 Cured for 40.0 min at 150°C |
| 7 Cured for 20.0 min at 150°C |
| 8 C 模具 |
|
【新闻资讯】查看全部
Westlake化学公司肯塔基州乙烯产能扩产
2016-01-14 Westlake化学公司计划扩产其位于肯塔基州的乙烯产能。计划在2017年上半年增加的产能为7000万磅/年。 Westlake的首席执行官兼总统Albert Chao表示“我们很高兴对于肯塔基州的乙烯产能扩产，至此扩产总量达到1亿磅/年，另外路易斯安那州也将在2016年第二季度扩产乙烯产能到2.5亿磅/年。 Westlake化学公司总部位于美国德克萨斯州休斯敦市，是基础化学品、乙烯基化学聚合物及其加工产品的纵向一体化生产厂商和全球范围内的供应商。< |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付