BMC 600成型化合物是一种矿物填充的玻璃纤维增强聚酯化合物,适用于压缩、转移和填充器注射成型。它是一种通用材料,具有中等的冲击强度和良好的综合电气性能。典型应用包括滑环、换向器和刷握。BMC 600模塑料是以各种工业颜色的挤压形式生产的。它可用于长度不超过12英寸的原木或作为特定重量的预切段塞,直径为1“至2½”。在这个范围内,较小的直径作为多个挤压件提供,重量公差为正负5%,最大正负15克。 BMC 600 molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a general purpose material with medium impact strength and good overall electrical properties. Typical applications include slip rings, commutators and brush holders. BMC 600 molding compound is produced in extruded form in a range of industrial colors. It is available in logs up to 12 inches in length or as precut slugs, of specific weight, in diameters from 1" to 2 ½". Within this range, smaller diameters are supplied as multiple extrusions and weight tolerances are plus or minus 5% up to a maximum of plus or minus 15 grams. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.01 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:模压成型 MD: Compression molding |
0.25 到 0.40 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.13 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
110 到 210 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,模压成型 1.8 MPa, unannealed, molded |
> 260 | ℃ | ASTM D648 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
6.40 mm 6.40 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
聚碳酸酯(PC)---5G、汽车、柔性电子及高性能薄膜等发展均离不开它
2020-09-15 搜料网资讯: 随着2019年6月6日工业和信息化部正式发放5G商用牌照,人们迎来了5G时代。工业和信息化部数据显示,2019年中国建成了13万个5G基站,预计到2020年底,5G基站将超过60万个, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |