说明:H 605是一种低熔融流速、高透明度的均聚物。这种树脂设计用于挤压和热成型。H 605具有优异的加工性能和高产量、优异的刚度/冲击强度平衡、较高的熔融强度、优异的光学性能和低气味/味道传递。应用:食品、化妆品、医疗保健和清洁产品的高透明度热成型包装;学校和办公室文件夹用的平板和波纹板。 H 605 is a low melt flow rate homopolymer with high transparency. This resin is designed for extrusion and thermoforming. H 605 exhibits excellent processability, high output, excellent stiffness/impact strength balance, high melt strength, outstanding optical properties and low odor/taste transfer. Applications: Highly transparent thermoformed packages for food, cosmetic, health care and cleaning products; Flat and corrugated sheets for school and office folders Processing: Thermoforming Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D792 |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
2.1 | g/10min | ASTM D1238 |
230℃,2.16kg 230℃,2.16kg |
2.1 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,注塑成型 23 ℃, injection molding |
3.2 | kJ/m² | ISO 180 |
23℃,注塑成型 23 ℃, injection molding |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
注塑薄膜 Injection molded film |
% | ISO 13468-1 | |
1000 µm,注塑成型 1000 µ m, injection molding |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
MPa | ASTM D638 | |
屈服,注塑成型 Yield, injection molding |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ASTM D638 | |
屈服,注塑成型 Yield, injection molding |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
1% 正割,注塑成型 1% cut, injection molding |
MPa | ISO 178 | |
1% 正割,注塑成型 1% cut, injection molding |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level 2 |
ISO 2039-2 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
对塑料袋征收额定费用 新西兰的“限塑令”呼声低落
2017-07-27 新西兰的消费者们在购物时不再购买塑料袋,这一举动对环保做出了巨大的贡献。如果我们的市长再推行收取政府支持的购物袋额外费用,保护环境的效果可能会更好。 从2009年4月以来,The Warehouse商店的塑料袋使用率已经下降了67%,因为从那时起每个塑料袋都要额外征收10c的费用。The Warehouse集团的环保倡议经理Greg Nelson形容购物袋的下降率“急速而又持久”。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |