| 牌号简介 About |
|---|
| SABIC® PP 576P是一种流动性能好、分子量分布窄的聚丙烯均聚物。由SABIC® PP 576P制成的产品通常具有低翘曲、高刚度以及室温下的中等冲击强度和高光泽。SABIC® PP 576P通常用于食品和非食品领域的瓶盖和瓶盖以及薄壁包装。本文所述产品尤其未经测试，因此未经验证可用于医药/医疗应用。 SABIC® PP 576P is a PP homopolymer grade that has good flow properties and a narrow molecular weight distribution. Products made from SABIC® PP 576P typically have low warpage, high stiffness in combination with moderate impact strength at room temperature and a high gloss. SABIC® PP 576P is typically used in caps & closures and thin wall packaging both in food and non-food segments. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
产品描述 Product Description
用途：包装;食品包装;护罩;外壳;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 均聚物; 低翘曲性; 窄分子量分布; 易流动; 表面光泽度好; Good Rigidity,Low warping,Good surface appearance,Good liquidity,Weight distribution,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.905 | g/cm³ | ASTM D792 , ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
19 | g/10min | ASTM D1238，ISO 1133 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
4.0 | kJ/m² | ISO 179/1eA |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
25 | J/m | ASTM D256-A |
|
23℃ 23℃ |
3.0 | kJ/m² | ISO 180-1A |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed 5 |
℃ | ISO 75-2/Bf | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/Af | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525 6 , ISO 306/A120 6 | |
|
B120 B120 |
℃ | ASTM D1525 7 , ISO 306/B120 7 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
|||
|
1% 正割 1% secant 3 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 4 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/1A/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/1A/50 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.039 in/min |
| 3 2.0 in/min |
| 4 testbar 80*10*4mm |
| 5 标准 B (120°C/h), 压 力1 (10N) |
| 6 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
生态环境部明确：七类树脂造粒产生的废料，不属于危险废物
2021-12-07 搜料网资讯： 近日，生态环境部公布《危险废物排除管理清单(2021年版)》，明确清单要求的固体废物不属于危险废物。 七类树脂生产过程中造粒工序产生的废料被列入清单，它们是：聚 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |