| 牌号简介 About |
|---|
| PETRONE GA501系列树脂是由客户选择的低密度聚乙烯颗粒衬里，用于薄膜挤出应用，需要良好的下拉和韧性。这些树脂具有优异的抗穿刺性、延伸率和热封强度。典型的应用包括重型运输袋，垃圾桶衬垫，商业和工业包装，以及食品和消费包装。 The Petrothene GA501 series of resins is pelletized linear low density polyethylene selected by customers for film extrusion applications that require excellent drawdown and toughness. These resins have excellent puncture resistance, elongation and heat seal strength. Typical applications include heavy duty shipping sacks, trash can liners, commercial and industrial packaging, as well as food and consumer packaging. GA501 is available without additives or fully formulated with slip and antiblock additives. |
产品描述 Product Description
用途：衬里;包装;袋子;工业应用;食品包装;
加工条件：薄膜挤出 Film extrusion
性能特点： 易剥离; 食品接触; 韧性好; 热封性好; 抗穿孔性; Good flexibility,Good heat sealing,Good dissection,Food contact compliance,Puncture Resistant
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness 2 |
|||
|
测试 test 2 |
25 | µm | |
|
割线模量 Secant modulus |
|||
|
1% 正割，TD，25 µm，吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
193 | MPa | ASTM D882 |
|
1% 正割，MD，25 µm，吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
186 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
|||
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
|||
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
|||
|
25 µm，吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
|
撕裂强度 tear strength |
|||
|
TD，25 µm，吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
|
MD，25 µm，吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，25.4 µm，吹塑薄膜 45 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
25.4 µm，吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blow（up Ratio） Blow（up Ratio） |
|||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Blow-Up Ratio: 2.5:1 |
|
【新闻资讯】查看全部 
Ascend：PA66短期内的供应受限
2018-10-12 尽管在全球供应严重紧张和需求强劲的情况下，原料成本不断下降，美国尼龙6和尼龙6,6（聚酰胺66-PA66）市场仍继续面临压力。 Ascend高性能材料公司（AscendPerformanceMaterials）总裁兼首席 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付