| 牌号简介 About |
|---|
| 产品说明HP4023W是一种低密度聚乙烯级产品，适用于生产通用薄膜，含有防滑和防堵添加剂。它具有优良的加工性能和光学性能，具有良好的机械性能。典型应用HP4023W可用于高清晰度洗衣袋、织物包装膜、生产袋、拉链袋。 Product Description HP4023W is Low Density Polyethylene grade suitable for producing general purpose films and contains slip and antiblock additives. It gives excellent processability and optical properties with good mechanical properties. Typical Applications HP4023W can be used for high clarity laundry bags, textile wrapping films, produce bags, zip lock bags. |
产品描述 Product Description
用途：薄膜;袋子;洗衣袋;
加工条件：吹塑薄膜
性能特点： 抗结块性; 高光滑性; 食品接触; 光学性能; 低密度; 易加工; Excellent Processability,Smoothness,Optical performance,High anti-blocking,Food contact compliance,Low density
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.923 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，21.6kg 190℃，21.6kg |
4.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
30 | µm | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD：30 µm，吹塑薄膜 1% secant, MD: 30 µ m, blow molded film |
60.0 | MPa | ASTM D882 |
|
1% 正割，TD：30 µm，吹塑薄膜 1% secant, TD: 30 µ m, blow molded film |
170 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服，30 µm，吹塑薄膜 MD, yield, 30 µ m, blow molded film |
MPa | ASTM D882 | |
|
TD，屈服，30 µm，吹塑薄膜 TD, yield, 30 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，30 µm，吹塑薄膜 MD : Break, 1.2 mil, Blown Film |
MPa | ASTM D882 | |
|
TD，断裂，30 µm，吹塑薄膜 TD, fracture, 30 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂，30 µm，吹塑薄膜 MD : Break, 1.2 mil, Blown Film |
% | ASTM D882 | |
|
TD，断裂，30 µm，吹塑薄膜 TD, fracture, 30 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
|||
|
30 µm，吹塑薄膜 30 µ m, blow molded film |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：30 µm，吹塑薄膜 MD: 30 µ m, blow molded film |
g | ASTM D1922 | |
|
TD：30 µm，吹塑薄膜 TD: 30 µ m, blow molded film |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，30 µm，吹塑薄膜 45 °, 30 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
30 µm，吹塑薄膜 30 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blow（up Ratio） Blow（up Ratio） |
|||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
用塑料薄膜添加空调的能耗
2017-08-19 在发达国家，空调负责总能耗的5%以上。随着印度和中国等大国继续发展，空调可能会更受欢迎。为了开发诸如传统空调机组的能源密集型热泵替代品，工程师们最近开始关注依靠建筑 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |