SABIC® LLDPE 726NJ是一种丁烯线性低密度聚乙烯树脂。这一牌号通常被设计为使吹塑薄膜具有相对较高的刚度,从而具有良好的可加工性和其他性能(如耐穿刺性、冲击强度和热密封性)的良好总体平衡性。该牌号不含TNPP。SABIC® LLDPE 726NJ的典型应用是运输袋、生产袋、罐衬和运输袋。SABIC® LLDPE 726NJ与低密度聚乙烯(15-85%)混合时具有良好的光学性能。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LLDPE 726NJ is a butene linear low density polyethylene resin. This grade is typically designed to give blown films a relatively high stiffness for good machinability and a good overall balance of other performance properties, such as puncture resistance, impact strength and heat sealability. The grade is TNPP free. Application Typical applications for SABIC® LLDPE 726NJ are shipping sacks, produce bags, can liners and carrier bags. SABIC® LLDPE 726NJ has good optical properties when blended with a LDPE (15-85%). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
220 | MPa | ISO 527-3 |
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
240 | MPa | ISO 527-3 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁冲击强度 Izod notched impact strength |
|||
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
抗穿刺性 Puncture resistance |
|||
吹塑薄膜,50.0 µm Blow molded film, 50.0 µ m |
J/m | 内部方法 | |
撕裂强度 tear strength 2 |
ISO 6383-2 | ||
MD,50 µm MD,50 µm |
kN/m | ISO 6383-2 | |
TD,50 µm TD,50 µm |
kN/m | ISO 6383-2 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部
衍生品助企业破洗牌困局 “互联网+”带来新机遇
2016-05-30 近年来,在原油大幅震荡的影响下,下游化工品价格波动较大,油价的每一次波澜都能牵动塑料产业的神经。当前,塑料产业存在宏观不景气、产能严重过剩等问题,企业不得不面对交易困难、融资难、融资成本高等制约因素。 在5月26日由大连商品交易所与中国石油和化学工业联合会、中国轻工业联合会联合主办的“2016中国塑料产业大会”上,业内人士指出,塑料行业洗牌呼之欲出,从宏观上看,产业结构调整和节能减排落地将是行业洗牌的分水岭。 与会人士表示,在供给侧改革的背景下,中下游企业只 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |