公司信息及水印
牌号简介 About |
---|
Hyflon F是一个独特的新型MFA聚合物家族,它结合了优异的机械特性和独特的性能,如化学惰性、高弯曲耐久性、固有阻燃性、低表面能和优异的介电性能。Hyflon® MFA® F1520是一种低熔融流速多用途树脂,具有优异的抗应力开裂性,连续工作温度高达225°C,100-150x10立方周期的弹性寿命(在0.3mm的FLIM上,ASTM D2176)。 Hyflon® F is a unique new family of PFA polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame resistance, low surface energy and exceptional dielectric properties. Hyflon® PFA F1520 is a low melt flow rate multi purpose resin with an exceptional stress crack resistance, continuous service temperature up to 225°C and a 100-150x10³ cycles flex-life (on a 0.3mm flim, ASTM D2176). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.10 到 2.15 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
372℃,5.0kg 372℃,5.0kg |
1.0 到 4.0 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
无断裂 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
265 到 275 | ℃ | ASTM D3307 |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
255 到 265 | ℃ | DSC |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
比热 specific heat |
|||
23℃ 23℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
|||
40℃ 40℃ |
W/m/K | ASTM C177 | |
结晶热 Crystallization heat |
J/g | DSC | |
融合热量 Fusion heat |
J/g | DSC | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 6 |
|||
1 mm 1 mm 6 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
23 ℃,50 Hz 23 ℃,50 Hz |
ASTM D150 | ||
23 ℃,100 kHz 23 ℃,100 kHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
23℃,50 Hz 23℃,50 Hz |
ASTM D150 | ||
23℃,100 kHz 23℃,100 kHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ASTM D3307 | |
拉伸强度 tensile strength 4 |
|||
断裂,23℃ Fracture, 23 ℃ 4 |
MPa | ASTM D3307 | |
拉伸应变 Tensile strain 4 |
|||
断裂,23℃ Fracture, 23 ℃ 4 |
% | ASTM D3307 | |
弯曲寿命 Bending life 5 |
Cycles | ASTM D2176 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.039 in/min |
3 2.0 in/min |
4 0.3mm 膜 |
5 50Hz |
【新闻资讯】查看全部
7月份化学原料和制品价钱同比下跌7.6%
2017-08-10 国家统计局8月9日发布的2017年7月份工业生产者出厂价格指数(PPI)数据显示,PPI环比上涨0.2%,同比上涨5.5%。其中,化学原料和化学制品价格环比下降0.1%,同比上涨7.6%。 2017年7月份,全国工业生产者出厂价格同比上涨5.5%,环比上涨0.2%。工业生产者购进价格同比上涨7.0%,环比持平。 工业生产者价格同比变动情况 工业生产者出厂价格中,生产资料价格同比上涨7.3%,影响工业生产者出厂 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |