PPE+PS,矿物,低翘曲,无卤阻燃剂, NORYL™ Resin ZM3640 - Asia is a Polyphenylene Ether + PS (PPE+PS) product filled with mineral. It can be processed by injection molding and is available in Asia Pacific. Typical application: Electrical/Electronic Applications. Characteristics include: Flame Rated Flame Retardant Halogen Free Warp Resistant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,2.16kg 300℃,2.16kg |
24 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 1 |
|||
屈服 yield 1 |
60.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
4.0 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
6.40 mm 6.40 mm |
4620 | MPa | ASTM D790 |
弯曲强度 bending strength |
|||
屈服,6.40 mm Yield, 6.40 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 0.20 in/min |
【新闻资讯】查看全部
丰喜华瑞论证碳酸二甲酯项目
2021-08-29 搜料网资讯: 8月16日,山西丰喜华瑞公司相关负责人前往山西中科惠安化工有限公司,就碳酸二甲酯项目与该公司董事长段礼、总经理姜伟及总工程师陈岩峰等进行交流。目前,华瑞公 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |