UBE超聚乙烯Umerit是以茂金属为催化剂,气相法合成的乙烯-α-烯烃共聚物。茂金属催化方法可以获得任何靶向分子结构,从而获得优良的物理性能。因此,Umerit2000F具有各种优良的性能。-加工时降低电机负载-高速拉伸时几乎不会发生拉伸共振。 UBE super polyethylene UMERIT® are ethylene alpha-olefin copolymers produced using metallocene catalyst by gas phase process. The metallocene catalytic method results in superior physical properties by being able to acquire any targeted molecular structures. Therefore UMERIT®2000F offer various excellent properties. -Reduced motor load at processing -Draw resonance at high-speed drawing hardly occurs |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
4.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
1000 | hr | ASTM D1693 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
104 | ℃ | ASTM D1525 |
熔融温度 Melting temperature |
116 | ℃ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
亨斯迈助意大利Forestali造皮革行业用复合资料
2016-03-04 意大利Industrie Chimiche Forestali S.p.A 公司利用亨斯迈的特等热塑性聚氨酯(简称TPU)研发了一种用于皮革制品的新型复合材料。 该复合材料被称为“Tintoretto”,采用双层TPU材质,能够增强高端皮革制品,例如设计师手袋和腰带的结构的完整性。 Forestali是皮革制品、制鞋、帆船和家具行业专用胶黏剂生产商,还生产多种类的浸染织物及纺织品。当觅得皮革产品市场的一处新商机时,Forestali随即联系了它的一个长期供应 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |