牌号简介 About |
---|
用于电线绝缘和电缆护套等应用中评估的非卤化阻燃柔性Noryl挤压级。优异的阻燃性能,拉伸伸长平衡,能够达到VW-1的性能和UL 1581规定的105C温度等级。肖氏硬度A。通常在标准挤压设备上进行的加工。使用0.12 mm x 20铜绞线对2.0 mm电线进行的UL 1581试验。 Non-halogenated flame retardant Flexible NORYL extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced tensile elongation, capable of VW-1 performance and 105C temperature rating as defined by UL 1581. 87 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0mm wire with 0.12mm X 20 stranded coppoer conductor. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
16 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -40.0 | ℃ | ASTM D746 |
UL温度额定值 UL temperature rating 7 |
105 | ℃ | UL 1581 |
Heat Deformation(121℃) Heat Deformation(121℃) 8 |
10 | % | UL 1581 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
2 mm,在油中 2 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
VW-1 VW-1 2 |
UL 1581 | ||
烟雾密度 Smoke density 9 |
|||
Flaming,Ds max:500.0 µm Flaming,Ds max:500.0 µm |
|||
Non-Flaming,Ds max:500.0 µm Non-Flaming,Ds max:500.0 µm |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,30 秒 Shore A, 30 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | UL 1581 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 4 |
MPa | UL 1581 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
% | UL 1581 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 5 |
% | UL 1581 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 6 |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
3. 类型 1, 50 mm/min |
4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
6. 13 mm/min |
7. 2.0mm wire with 0.12 mm x 20 stranded copper |
8. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
9. Plaque |
【新闻资讯】查看全部
场外期权逐步失掉塑料企业认可
2017-06-20 满足个性化避险需求 6月17日,华泰期货在广州举办“羊城荟(第九期)塑料化工行情研讨会”。与会嘉宾表示,塑料行业整体利润率较低,对原材料价格比较敏感。随着价格不断波动,塑料企业风险管理的诉求愈加强烈,与期货联系会更加紧密。与此同时,风险管理公司从企业自身情况出发,设计个性化产品,受到了越来越多产业客户的关注。 “塑料制造业属于微利行业,去年整个行业的利润率在6.1%―6.2%,广东地区利润率为5.8%,在国内制造业中处于低位 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |