Flexirene® FG 23 F是一种含抗氧化剂的丁烯共聚物线性低密度聚乙烯(C4-LLDPE),适用于吹塑薄膜挤出。Flexirene® FG 23 F代表了flexinene fg 20 f的防滑和防堵剂版本。主要应用Flexirene® FG 23 F推荐用于一般用途薄膜、工业内衬和购物者的生产;建议在混合和与ldpe共挤时使用。 Flexirene FG 23 F is a butene copolymer linear low density polyethylene (C4-LLDPE) with antioxidants, suitable for blown film extrusion. Flexirene FG 23 F represents the version with slip and antiblock agents of Flexirene FG 20 F. Main Application Flexirene FG 23 F is recommended for the production of general purpose film, industrial liners and shoppers; its use is suggested both in blend and in coextrusion with LDPE. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
0.14 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
薄膜厚度 film thickness |
15 to 50µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD:25.0 µm MD:25.0 µm |
kN/m | ISO 6383-2 | |
TD:25.0 µm TD:25.0 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Blown Film |
【新闻资讯】查看全部
40家钛白粉企业霸气暴跌!
2018-03-07 进入2018年,钛白粉的“好日子”就来了,龙头企业纷纷开启连番涨价模式。 国内外钛白粉市场形势一片大好,涨价信息已经将近40家!并且还在陆续增加中...... 下面涨价信息根据调价日期整理 日本石原 1月1日起,亚太地区钛白粉价格上调200美元/吨(合人民币1308.5元/吨) 科慕 1月1日起,大中华区销售的Ti-Pure钛白 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |