牌号简介 About |
---|
TC-857 A/B是一种坚硬的84邵尔D聚氨酯系统,具有优异的物理性能。它是一种高性能材料,具有高的热变形能力和低收缩率。TC-857是一种透明的铸造材料,允许不受限制的着色和精确的颜色匹配。本产品非常适合生产需要非喷漆表面的本色零件。这个系统可以很容易地用手或与计量混合配药,压力或真空铸造设备处理。产品亮点:热变形温度高,抗冲击性好,无臭,清晰;易于着色或着色,适合手工、真空或压力铸造,透明度高。 TC-857 A/B is a rigid 84 Shore D polyurethane system that exhibits exceptional physical properties. It is a high performance material that features high heat deflection capability and low shrinkage. TC-857 is a clear casting material that allows for unrestricted tinting and precise color matching. This product is ideal for producing intrinsically colored parts requiring a non-painted finish. This system can be easily processed by hand or with meter-mix-dispense, pressure or vacuum cast equipment. Product Highlights: Exhibits high heat distortion temperature Excellent impact resistance Odorless, clear; easy to tint or color Excellent for hand, vacuum or pressure casting Exceptional clarity |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
50 | J/m | ASTM D256 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
25℃ 25℃ |
5.0 到 7.0 | day | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
82 到 86 | ASTM D2240 | |
拉伸模量 Tensile modulus |
2000 | MPa | ASTM D638 |
拉伸强度 tensile strength |
62.7 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
Part A Part A |
|||
Part B Part B |
|||
密度 Density |
g/cm³ | ASTM D792 | |
收缩率 Shrinkage rate 2 |
|||
MD:12.7 mm MD:12.7 mm 2 |
% | ||
颜色 colour |
|||
Part A Part A |
|||
Part B Part B |
|||
布络克菲尔德粘度 Brookfield viscosity |
|||
混合 blend |
Pa·s | ||
Part A,25℃ Part A,25℃ |
Pa·s | ||
Part B,25℃ Part B,25℃ |
Pa·s | ||
Part B,32℃ Part B,32℃ |
Pa·s | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
wk | ||
脱模时间 stripping time |
|||
25℃ 25℃ |
min | ||
胶凝时间 Gelation time |
min | ||
工作时间 working hours 3 |
|||
25℃ 25℃ 3 |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 12x0.5x0.5 in |
3 100g mass |
【新闻资讯】查看全部
埃克森美孚化工推出全新埃能宝™ 茂金属聚乙烯树…
2016-04-21 ・ 结合了出色的挺度、强度和夹持力等特性,同时具备优异的收缩性能 ・ 具备卓越的牢固集束性能和均衡的收缩性能,使包装安全紧固 ・ 提供高达 25% 的减薄机会 ・ 具有出众的光学效果,可提高零售货架吸引力 休斯顿(2016年4月20日)- 埃克森美孚化工为旗下埃能宝™ 产品线推出了最新的优化解决方案:埃能宝™ 40-02 茂金属聚乙烯 (mPE) 树脂。利 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |