| 牌号简介 About |
|---|
| 特性：高粘度基产品应用：单丝在热变形温度（熔点接近40°C）下比PA 12的优势拉伸和弯曲强度在高湿强度下表现突出的回收率Vestamid D系列的PA 612化合物因此代表了特殊产品维他明L系列PA 12化合物的综合筛选。 Characterization: high-viscosity base product Applications: monofilaments Its advantages over PA 12 exhibit in the heat deflection temperature (melting point nearly 40 °C higher) tensile and flexural strength outstanding recovery at high wet strength The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
产品描述 Product Description
用途：单丝;
颜色：自然色,黑色
加工条件：挤出 Extrusion
性能特点： 防火阻燃等级HB; 耐磨; 耐油; 高粘度; 耐化学性; 食品接触; 冲击性能好; 抗应力开裂; 耐燃油; High impact resistance,High Viscosity,Food contact compliance,Good wear resistance,Grease resistance,Solvent resistance,High ESCR,Fuel resistance,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.06 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate 2 |
ISO 294-4 | ||
|
TD TD |
1.5 | % | ISO 294-4 |
|
MD MD |
1.6 | % | ISO 294-4 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
2.7 | % | ISO 62 |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
1.0 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/1A | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/1A | |
|
屈服 yield |
% | ISO 527-2/1A | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃，完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
|
23℃，完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ISO 75-2/B | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed 3 |
℃ | ISO 75-2/B | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
热变形温度 Hot deformation temperature |
ISO 75-2/A | ||
|
1.8 MPa，未退火 1.8 MPa, unannealed 7 |
℃ | ISO 75-2/A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
|
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：23~55℃ MD：23~55℃ |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index 5 |
|||
|
解决方案 A Solution A |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
电解腐蚀 Electrolytic corrosion |
IEC 60426 | ||
|
ISO Shortname ISO Shortname |
ISO 1874 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 measured at specimen 60x60x2mm |
| 3 after conditioning at 180 °C / 60 min |
| 4 2nd Heating |
| 5 50 drops Value |
|
【新闻资讯】查看全部 
塑料摩擦系数ASTM D3702
2017-07-03 使用推力垫圈试验机磨损率和摩擦系数ASTM D3702 范围： 该测试方法评估最终使用类型条件下摩擦接触材料的性能。触点可以是针对钢材或对自身的测试材料。测试规范是指自润滑材料 |
|