牌号简介 About |
---|
Baydul- 660 IBS是一种用于反应注射成型(RIM)工艺的黑色、硬质聚氨酯结构泡沫体系。该系统包括一个专门设计的交互式吹扫系统(IBS),作为两个反应性液体成分提供。A组分是一种聚合物二苯基甲烷二异氰酸酯(PMDI),B组分是一种不含CFC-或HCFC发泡添加剂的配方多元醇体系。注意:由于可能存在颜料沉淀,在将桶中的内容物输送到日计量箱之前,应彻底搅动成分B。Baydur 660 IBS系统是为通用应用而设计的,用于工业和娱乐市场。这些应用通常利用了材料的强度、优异的表面光洁度和大零件性能。与任何产品一样,在给定应用中使用Baydur 660 IBS系统必须由用户提前进行测试(包括现场测试等),以确定适用性。 Baydur 660 IBS is a black-pigmented, rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Compo- nent B is a formulated polyol system containing no CFC- or HCFC-blowing additives. Note: Component B should be agitated thoroughly prior to delivery of contents of the drum to the day tank due to possible pigment settling. The Baydur 660 IBS system was designed for general-purpose applications and is used in industrial and recreational markets. The applications typically take advantage of the material's strength, excellent surface finish, and large part capability. As with any product, use of the Baydur 660 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.479 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:6.35 mm MD:6.35 mm |
0.30 到 0.50 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
内部方法 | ||
-- -- 2 |
8.8 | kJ/m² | 内部方法 |
-- -- 3 |
9.0 | kJ/m² | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D,6.35 mm Shaw D, 6.35 mm |
55 | ASTM D2240 | |
邵氏 D,12.70 mm Shore D, 12.70 mm |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
MPa | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
压缩强度 compressive strength |
ASTM D695 | ||
6.35 mm 6.35 mm |
MPa | ASTM D695 | |
12.7 mm 12.7 mm |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.35 mm 0.45 MPa, unannealed, 6.35 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,12.7 mm 0.45 MPa, unannealed, 12.7 mm |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.5 |
3 0.25 in |
【新闻资讯】查看全部
宝马经过3D打印方法消费了一百万个零件
2018-11-20 在宝马集团,3D打印部件的使用正在不断增加。仅在过去十年中,宝马就通过3D打印这种创新方法生产了一百万个零件。而今年宝马集团增材制造中心的3D打印部件产量预计将超过20万个,比去年同比增长42%。 宝马集团增材制造中心主任Jens Ertel博士说:“目前,在车辆批量生产中,增材制造部件的使用量正在大幅上升。我们密切关注这些制造方法的先进开发和应用,例如与该领域的领先制造商保持长期合作。与此同时,我们也正在进行有针对性的技术研究和创新生产系统评估。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |