牌号简介 About |
---|
Nylene® PX1719HS是一种热稳定、高冲击、尼龙6挤出级树脂,具有低弯曲模量。PX1719HS非常适用于需要卓越韧性和灵活性的管材和型材的挤压。由于其优良的流动特性,它也可用于注射成型零件,要求高的伊兆欧冲击值。最佳加工条件应在模具或喷嘴处提供520-540°F的熔化温度。 Nylene PX1719HS is a heat stabilized, high impact, nylon 6 extrusion grade resin with a low flexural modulus. PX1719HS is ideally suited for extrusion of tubing and profiles requiring outstanding toughness and flexibility. Because of its excellent flow characteristics, it may also be used for injection molding parts requiring a high Izod impact value. Optimum processing conditions should provide a melt temperature of 520 - 540°F at the die or nozzle. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
62.1 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
250 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
655 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
850 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
赢创加入MIT-IBM沃森人工智能实验室,借助AI技术推进创新
2021-04-20 搜料网资讯: ●赢创、IBM研究中心与麻省理工学院(MIT)携手探索行业潜在数字化应用 ● 赢创加入研究项目顾问委员会 ●赢创提前延长与IBM的战略伙伴合作协议 赢创与IBM正扩大在数字 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |