牌号简介 About |
---|
EBA Alcudia PA-1770是一种适用于一般挤出、注塑和需要良好加工性、柔韧性和良好机械性能的化合物的共聚物。丙烯酸丁酯含量为17%。它含有抗氧化添加剂。典型应用挤出(型材、片材)注射成型微孔泡沫化合物和母料电缆推荐的熔融温度180°C。EBA共聚物具有良好的热稳定性,可在需要时提高加工温度。PA-1770的加工特性与低密度聚乙烯相似,推荐使用传统的聚乙烯挤出机。各生产线的加工条件应得到优化。 EBA ALCUDIA® PA-1770 is a copolymer suitable for general extrusion, injection moulding and compounds where good processability, flexibility and very good mechanical properties are required. The butyl acrylate content is 17%. It contains antioxidant additives. TYPICAL APPLICATIONS Extrusion (profiles, sheets) Injection moulding Microcellular foams Compounds and masterbatches Cables Recommended melt temperature 180°C. EBA copolymers exhibit excellent thermal stability, which allows higher processing temperatures if needed. Processing characteristics of PA-1770 are similar to LDPE and conventional polyethylene extruders are recommended. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
7.0 | g/10min | ISO 1133 |
丁酯丙烯酸成分 Butyl acrylate composition |
17.0 | wt% | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
90 | ISO 868 | |
邵氏 D Shaw's D |
33 | ISO 868 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
应急管理部:2021年化工和危险品领域安全生产形势总体稳定
2022-01-20 搜料网资讯: 1月20日应急管理部举行新闻发布会,通报2021年全国安全生产和自然灾害形势,发布2021年全国应急救援、生产安全事故十大典型案例。 2021年,全国各种自然灾害共造成1. |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |