牌号简介 About |
---|
Escorene Ultra LD 701.ID是一种小数熔融指数,含有10.1%(质量分数)醋酸乙烯酯的共聚物特种薄膜树脂,用于有高热封性、高强度和高韧性(特别在低温下)要求的用途。 Escorene Ultra LD 701.ID is a fractional melt index, 10.1 wt% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength, and toughness, particularly at low temperatures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.932 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.19 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
10.1 | wt% | ExxonMobil Method |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
1% 正割,TD 1% secant, TD |
121 | MPa | ASTM D882 |
1% 正割,MD 1% secant, MD |
107 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂 TD, fracture |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD TD |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
习近平出席亚太经合组织工商领导人峰会并发表主旨演讲
2021-11-11 搜料网资讯: 11月11日,国家主席习近平应邀在北京以视频方式向亚太经合组织工商领导人峰会发表题为《坚持可持续发展 共建亚太命运共同体》的主旨演讲。 习近平指出,当前,新冠 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |