| 牌号简介 About |
|---|
| 168S是以磷、溴、锑为阻燃剂的低卤环保型聚丙烯。通过固化相和气相机理提高阻燃性能，并通过催化机理加速熔滴，发挥阻燃性能。168s可燃性可达到UL 94V-2（1.5mm和3.0mm），灼热丝试验符合GWIT:775/3.0和GWFI:850/3.0。168S通过了UL认证，满足了RoHS、SVHC、PFOS&PFOA、16P、PAHS等要求，具有成品密度低、烟度低、对模具腐蚀小等特点。 168S is low halogen flame retardant environmental polypropylene with phosphorus, bromine and antimony as the flame retardant elements. Through solidifying phase and gas-phase mechanism improve flame retardant performance, and accelerating melting and dripping by catalytic mechanism to play flame retardant perforamnce. 168S flammability can reach UL 94 V-2 (1.5mm and 3.0mm), glow-wire test meets GWIT:775/3.0 and GWFI:850/3.0. 168S has passed UL certification, and meet the requiements of RoHS, SVHC, PFOS & PFOA, 16P, PAHs...etc. 168S has characteristics of finished products low density, low smokes, less corrosion to molds...etc. |
产品描述 Product Description
用途：电气元件;电气/电子应用领域;
性能特点： 低烟; 机械强度好; 阻燃; 韧性好; 低密度; Good Rigidity,Good flexibility,Low smoke,Flame Characteristics,Low density
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.970 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
5.0 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
1.1 到 1.5 | % | ASTM D955 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
33.0 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
50 | % | ASTM D638 |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
|||
|
3.00 mm 3.00 mm |
|||
|
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 2、Phosphorus, Bromine and Antimony |
|
【新闻资讯】查看全部
模具行位留意要点
2016-07-12 所谓模具行位指的是模具的行位机构,即凡是能够获得侧向抽芯或侧向分型以及复位动作来拖出产品倒扣,低陷等位置的机构。其利用成型的开模动作用,使斜撑梢与滑块产生相对运动趋势,使滑块沿开模方向及水平方向的两种运动形式,使之脱离倒勾。那关于模具行位要注意哪些要点呢? 模具行位应注意十大要点: 1、一般用斜导柱作动力,比较小的抽芯距用T形槽,大于30mm用油缸抽芯。 2、斜导柱的角度比铲机角度小2―3度。 3、后模行位伸入前模超过总高度一 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付