| 牌号简介 About |
|---|
| Greenflex® FD 20是一种乙烯-醋酸乙烯共聚物（EVA），适用于吹塑薄膜挤出。Greenflex® FD 20薄膜具有良好的光学性能、高抗冲击性、拉伸强度、断裂伸长和低蠕变。主要用途Greenflex® FD 20推荐用于食品包装的热收缩膜和多层拉伸膜，包括深冷冻食品包装。 Greenflex FD 20 is an ethylene vinyl acetate copolymer (EVA) suitable for blown film extrusion. Films produced by Greenflex FD 20 exhibit good optical properties, high impact resistance, tensile strength, elongation at break and low creep. Main Application Greenflex FD 20 is recommended for thermo-shrinkable films and multilayer stretch films for food packaging, included deep-frozen food packaging. |
产品描述 Product Description
用途：薄膜;多层薄膜;收缩性薄膜;食品包装;拉伸缠绕;
加工条件：吹塑薄膜
性能特点： 拉伸性能好; 共聚物; 食品接触; 冲击性能好; 光学性能; 韧性好; Good flexibility,High impact resistance,Optical performance,Food contact compliance,Good Tensile Strength,Copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.924 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.50 | g/10min | ISO 1133 |
|
醋酸乙烯含量 Vinyl acetate content |
5.0 | wt% | Internal Method |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ISO 868 | ||
|
邵氏 A，注塑成型 Shaw A, injection molding |
95 | ISO 868 | |
|
邵氏 D，注塑成型 Shaw's D, injection molding |
44 | ISO 868 | |
|
摩擦系数 friction coefficient |
|||
|
与自身 - 动态，吹塑薄膜 Self dynamic, blow molded film |
ISO 8295 | ||
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
1% 正割，MD，吹塑薄膜 1% secant, MD, blow molded film |
MPa | ISO 527-3 | |
|
1% 正割，TD，吹塑薄膜 1% secant, TD, blow molded film |
MPa | ISO 527-3 | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，吹塑薄膜 MD, yield, blow molded film |
MPa | ISO 527-3 | |
|
TD，屈服，吹塑薄膜 TD, yield, blow molded film |
MPa | ISO 527-3 | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，断裂，吹塑薄膜 MD, fracture, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，吹塑薄膜 TD, fracture, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，吹塑薄膜 MD, fracture, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，吹塑薄膜 TD, fracture, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact 2 |
|||
|
吹塑薄膜 Blown film 2 |
g | ISO 7765-1/A | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
|
MD MD |
kN/m | ISO 6383-2 | |
|
TD TD |
kN/m | ISO 6383-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，吹塑薄膜 45 °, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
吹塑薄膜 Blown film |
% | ISO 14782 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
| 3 Blown Film |
|
【新闻资讯】查看全部 
晓星越南第2套PP装置投产！在越南PP产能已扩至60万吨/年
2021-09-08 搜料网资讯： 近日，韩国晓星化学宣布，该公司投资1.5万亿韩元建设的聚丙烯(PP)工厂投入商业化生产，储存原料液化石油气(LPG)的储罐和加工设施也将同时投入使用。晓星化学通过此举 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付