牌号简介 About |
---|
Ultramid® 8202C是一种改性结晶低粘度PA6注塑均聚物。它还提供热稳定(Ultramid® 8202C hs)和/或色素版本。其独特的晶体结构使其作为均聚物的强度、刚度、热变形温度和负载性能得到提高。它还可以更快地循环,同时保持性能和耐化学性。应用程序Ultramid® 8202C非常适合应用程序,例如:家具脚轮、齿轮、窗五金件和配件、绝缘体、衬套、阀门、继电器、布线设备和其他电气组件。 Ultramid 8202C is a modified crystalline and low viscosity, PA6 injection molding homopolymer. It is also available in heat stabilized (Ultramid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and chemical resistance. Applications Ultramid 8202C is ideally suited for applications such as: furniture casters, gears, window hardware, and fittings, insulators, bushings, valves, relays, wiring devices, and other electrical components. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D792 |
密度 Density |
1.13 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.90 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
9.3 | % | ISO 62 |
饱和 saturated |
9.3 | % | ASTM D570 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
24hr 24hr |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
6.0 mm 6.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
6.0 mm 6.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
6.0 mm 6.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 2 |
|||
1.5 mm 1.5 mm 2 |
kV/mm | ASTM D149 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.71 mm 0.71 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
|||
23℃ 23℃ |
J | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
-40℃ -40℃ |
MPa | ISO 527-2 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
80℃ 80℃ |
MPa | ISO 527-2 | |
120℃ 120℃ |
MPa | ISO 527-2 | |
150℃ 150℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服,-40℃ Yield, -40 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,80℃ Yield, 80 ℃ |
MPa | ASTM D638 | |
屈服,121℃ Yield, 121 ℃ |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服,-40℃ Yield, -40 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
屈服,80℃ Yield, 80 ℃ |
MPa | ISO 527-2 | |
屈服,120℃ Yield, 120 ℃ |
MPa | ISO 527-2 | |
屈服,150℃ Yield, 150 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
屈服,-40℃ Yield, -40 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,80℃ Yield, 80 ℃ |
% | ASTM D638 | |
屈服,121℃ Yield, 121 ℃ |
% | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
ISO 527-2 | ||
-40℃ -40℃ |
% | ISO 527-2 | |
23℃ 23℃ |
% | ISO 527-2 | |
80℃ 80℃ |
% | ISO 527-2 | |
120℃ 120℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
23℃ 23℃ |
MPa | ISO 178 | |
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
23℃ 23℃ |
MPa | ISO 178 | |
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
断裂,-40℃ Fracture, -40 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ASTM D638 | |
断裂,121℃ Fracture, 121 ℃ |
MPa | ASTM D638 | |
断裂,-40℃ Fracture, -40 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ |
% | ASTM D638 | |
断裂,121℃ Fracture, 121 ℃ |
% | ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
一季度我国煤炭、原油、天然气进口均同比下降
2022-04-20 4月18日电 据国家统计局官网公布的数据,一季度,进口煤炭5181万吨,同比下降24.2%;进口原油12785万吨,同比下降8.1%;进口天然气2782万吨,同比下降5.1%。 3月份,规模以上工业主要能 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |