Hostacom TKC 2007N D12899是一种5%滑石填充的聚丙烯共聚物,具有低密度、高温下良好的耐初花性、很好的冲击/刚度平衡、很好的可塑性和优异的耐刮擦性。先进的技术使矿物填料的含量大大降低,这有助于减少最终零件的重量。有关收缩建议,请联系LyondellBasell。本产品还提供其他颜色,可根据客户要求开发新颜色。 Hostacom TKC 2007N D12899 is a 5% talc filled PP copolymer, with low density, excellent blooming resistance at elevated temperatures, very good impact/stiffness balance, very good mouldability and excellent scratch resistance. Advanced technologies allowed for a significant reduction of mineral filler content which contributed to the reduction of final part weight. Please contact LyondellBasell for shrinkage recommendations. This product is also available in other colors, new colors can be developed depending on customer requirements. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
16 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
20.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
4.8 | % | ISO 527-2 |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
1650 | MPa | ISO 178-A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 |
备注 |
---|
2. 1.0 mm/min |