牌号简介 About |
---|
Zylar 960是一种冲击改性的苯乙烯-丙烯酸共聚物,具有相当于某些等级聚碳酸酯的韧性、良好的透明度和优越的加工特性,适用于要求高的注塑应用。具有特殊的韧性,低密度,易于加工,伽马和ETO可灭菌,符合USP XXIII第六类塑料应用,电器和消费品,医疗器械,玩具,办公用品,工业外壳和盖子规范。 Zylar® 960 is an impact modified styrene acrylic copolymer that provides toughness equivalent to some grades of polycarbonate, good clarity and superior processing characteristics for demanding injection molded applications. FEATURES Exceptional toughness Low density Ease of processing Gamma & ETO sterilizable Meets USP XXIII specifications for Class VI plastics APPLICATIONS Appliances and consumer goods Medical devices Toys Office accessories Industrial housings and covers |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
6.0 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
200℃,5 kg 200℃,5 kg |
6.00 | cm³/10min | |
220℃,10 kg 220℃,10 kg |
65.0 | cm³/10min | |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 到 0.60 | % | ASTM D955 |
-- -- |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ASTM D570,ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
落锤冲击 Drop hammer impact |
J | ASTM D5420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/B | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 1 | |
B50 B50 |
℃ | ISO 306 | |
最高使用温度 Maximum operating temperature |
℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
|||
-- -- 2 |
ASTM D542 | ||
-- -- |
ISO 489 | ||
透光率 Transmittance |
|||
550 nm 550 nm |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
R 级 R-level |
ISO 2039-2 | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
-- -- |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4h/80°C |
3 标准 B (120°C/h), 压 力1 (10N) |
4 Sodium D Line |
【新闻资讯】查看全部
行业提示:儿童玩具分散包装存在窒息隐患
2016-04-21 随着科技的发展和生产工艺的进步,儿童玩具在功能越来越多的同时,小零件也越来越多。商家为了方便运输,往往将玩具部件分散包装,然后由家长组装后给孩子玩耍。在家长拆开包装组装玩具时,就可能产生新的安全隐患。日前,记者从国家质检总局了解到,因为玩具存在安全隐患,广州、上海等地12家玩具生产企业按照《儿童玩具召回管理规定》的要求,在全国范围内对12批次存在缺陷的玩具产品(含童车)实施召回。除了玩具本身的质量外,童车类产品都是因为包装不符合规定而被召回。医学专家提醒市民,玩具外包装的塑料薄膜会吸附在儿 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |