| 牌号简介 About |
|---|
| Riblene® FL 23 I是一种添加了滑动剂的低密度聚乙烯（LDPE），是吹塑薄膜挤出的理想选择。Riblene® FL 23 I的特点是工艺性和机械性能之间的良好平衡。用Riblene® FL 23 I制造的薄膜容易热收缩，具有良好的光学和机械性能。主要应用Riblene® FL 23 I推荐用于一般吹塑薄膜应用，用于生产低规格薄膜和收缩膜，用于层压和混合。 Riblene FL 23 I is a low density polyethylene (LDPE) additivated with slip agent, ideal for blown film extrusion. Riblene FL 23 I is characterised by a good balance between proc-essability and mechanical properties. Films manufactured with Riblene FL 23 I are easily heat shrinkable and characterised by good optical and mechanical properties. Main Applications Riblene FL 23 I is recommended for general blown film applications, for the production of low gauge film and shrink film, for lamination and for blending. |
产品描述 Product Description
用途：薄膜;收缩性薄膜;层压板;吹膜;混合;
加工条件：吹塑薄膜
性能特点： 热收缩性好; 高光滑性; 食品接触; 光学性能; 低密度; 易加工; Excellent Processability,Smoothness,Optical performance,Food contact compliance,Low density,Good thermal contraction
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.923 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.2 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient |
|||
|
与自身 - 动态，吹塑薄膜 Self dynamic, blow molded film |
0.13 | ISO 8295 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
40 | µm | |
|
薄膜厚度 film thickness |
25 to 80 µm | ||
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
1% 正割，MD，40 µm，吹塑薄膜 1% secant, MD, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
1% 正割，TD，40 µm，吹塑薄膜 1% secant, TD, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，40 µm，吹塑薄膜 MD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，屈服，40 µm，吹塑薄膜 TD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact 2 |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film 2 |
g | ISO 7765-1 | |
|
撕裂强度 tear strength 3 |
ISO 6383-2 | ||
|
MD，40 µm MD，40 µm |
kN/m | ISO 6383-2 | |
|
TD，40 µm TD，40 µm |
kN/m | ISO 6383-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，40.0 µm，吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 | |
| 备注 |
|---|
| 2 F50 |
| 3 Blown Film |
|
【新闻资讯】查看全部
且看塑膜产业链近期的五大热点
2016-03-18 在行业发展的拐点上，作坊式、粗放型、科技含量低下的企业必然会被淘汰，能够把握市场先机和适应社会发展的创新型、功能性薄膜企业将迎来新一轮的发展浪潮。pvc膜行业产能化显成效，引起塑料薄膜业“寒潮”涌动下的思考。 去产能显成效，西北企业话语权提升 在国家化解过剩产能的重大决策下，PVC行业去产能化显成效，2016年市场价格持续上涨，西北PVC生产企业积极降本增效，市场定价话语权提升。 关注电石法PVC企业标的：君 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付