牌号简介 About |
---|
FRIANYL® A3 RV0是一种未填充的聚酰胺66(尼龙66)化合物,热稳定,阻燃,无卤素和红磷,UL认证的V0。经VDE认证。还根据铁路要求EN45545-2和NFF 16-101进行认证。该化合物用于注塑成型。FRIANYL® A3 RV0主要为电气和电子工业设计。它也适用于汽车或工业和消费者应用。 FRIANYL® A3 RV0 is an unfilled Polyamide 66 (Nylon 66) compound, heat stabilized, flame retardant, halogen and red phosphorous free, UL listed V0. It is VDE certified. It is also certified according to railways requirements EN45545-2 and NFF 16-101. This compound is intended for injection molding. FRIANYL® A3 RV0 is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive or Industrial & Consumer applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.160 | g/cm³ | ISO 1183 |
成型收缩率 Forming shrinkage rate |
|||
流动 flow |
1.2-1.6 | % | ISO 294-4,257 |
横向 transverse |
1.2-1.6 | % | ISO 294-4,257 |
吸水率 Water absorption rate |
|||
23℃ 23℃ |
7.4 | % | ISO 62 |
温度吸收 Temperature absorption |
|||
23°C/50%RH 23°C/50%RH |
2.1 | % | ISO 62 |
粘度数 Viscosity number |
|||
PA硫酸 PA sulfuric acid |
ml/g | ISO 307 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-1,-2 | |
拉伸应力 Tensile stress |
|||
屈服50mm/min Yield 50mm/min |
MPa | ISO 527-1,-2 | |
拉伸应变 Tensile strain |
|||
屈服50mm/min Yield 50mm/min |
% | ISO 527-1,-2 | |
断裂50mm/min Fracture 50mm/min |
% | ISO 527-1,-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23°C 23°C |
kJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23°C 23°C |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
|||
20°C/min 20°C/min |
℃ | ISO 11357-1/-3 | |
负载下的热变型温度 Thermal deformation temperature under load |
|||
1.8 MPa 1.8 MPa |
℃ | ISO 75-1,-2 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1,-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
FMVSS FMVSS |
ISO 3795 | ||
可燃性 Flammability |
|||
厚度3.2mm Thickness 3.2mm |
class | UL 94 | |
厚度1.6 mm Thickness 1.6 mm |
class | UL 94 | |
厚度0.8 mm Thickness 0.8 mm |
class | UL 94 | |
厚度0.4 mm Thickness 0.4 mm |
class | UL 94 | |
测试厚度 Test thickness |
|||
h h |
mm | UL 94 | |
UL识别 |
|||
h h |
UL 94 | ||
灼热丝易燃指数 Burning wire flammability index |
|||
0.8mm 0.8mm |
℃ | IEC 60695-2-12 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
球压测试 Ball pressure test |
℃ | IEC 60695-10-2 | |
连续工作温度 Continuous operating temperature |
℃ | DIN/IEC 60216-1 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23°C 23°C |
ohm·m | IEC 62631-3-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
UL 746 | ||
|
IEC 60112 | ||
CTI CTI |
|||
50滴 50 drops |
V | IEC 60112 | |
100滴 100 drops |
V | IEC 60112 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20000 hr |
3 23°C |
【新闻资讯】查看全部
4月国内汽车产销量接近腰斩,部分车企产能损失超六成
2022-05-12 这个春天,汽车产业感受到近十年来都未有的寒意。 5月11日,中汽协会公布4月汽车工业运行数据。数据显示,4月,乘用车销量为96.5万辆,同比下降43.4%,环比分别下降48.2%。与刚刚过 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |