具有高流动性的阻燃ABS材料,可应用于显示器、打印机、传真机、复印机等办公自动化设备的外部材料。 Starex VH-0800 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Starex VH-0800 include appliances and electrical/electronic applications. Characteristics include: Flame Rated Flame Retardant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
- - |
1.17 | g/cm³ | ISO 1183 |
|
1.17 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
5.4 | g/10min | ASTM D1238 |
200℃,5.0kg 200℃,5.0kg |
5.4 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:3.2 mm TD:3.2 mm |
0.33 to 0.40 | % | ASTM D955 |
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ISO 2577 | |
MD:3.2 mm MD:3.2 mm |
% | ISO 2577 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 5 |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ 5 |
kJ/m² | ISO 180-1A | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ISO 75-2/A | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/A | |
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ISO 75-2/B | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,4.0 mm 0.45 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 0.11 in/min |
4 0.079 in/min |
5 Thickness: 4mm |
【新闻资讯】查看全部
巴斯夫、陶氏化学、杜邦、孟山都等企业二季度业绩
2017-09-20 欧洲 世界最大化工企业巴斯夫(BASF)今年第二季度的销售额和税前盈利分别高达163亿欧元和23亿欧元,销售额同比增长12%,利润超过预期。基础化工和油气部门的需求强劲,推高了盈利水平。 林德集团(The Linde Group)公布2017年上半年业绩。上半年营收86.53亿欧元,上年同期为82.64亿欧元。上半年营业利润21.23亿欧元,上年同期为20.36亿欧元。本期利润6.56亿欧元,上年同期为6.80亿欧元。 赢创工业集团(Evon |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |