公司信息及水印
牌号简介 About |
---|
Marlex® HMN TR-938是一种中密度聚乙烯材料,。 该产品在北美洲或拉丁美洲有供货,加工方式为:滚塑成型。 Marlex® HMN TR-938的主要特性有: 阻燃/额定火焰 己烯共聚单体 紫外线稳定 耐冲击 良好的抗紫外线能力 典型应用领域包括: 容器 户外应用 汽车行业 海洋应用 罐子 These hexene copolymers are tailored for rotational molding applications that require: Wide process window Excellent impact strength Good flow Excellent ESCR Typical applications for HMN TR-938 and HMN TR-938G include items such as: Industrial waste containers and tanks Marine equipment Industrial tanks These resins are available in: Pellet form - HMN TR-938 35 US mesh powder - HMN TR-938G These resins meet these specifications: ASTM D4976 - PE 223 FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c) Table 2. Single use articles contacting food types I, II, IV-B, VI-A, VI-B, VII-B, and VIII. Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1. UL94HB yellow card per UL file E349283 UL746C (f1) yellow card per UL file E349283 FMVSS.302 burn test AS/NZS 4020:2005 (contact with drinking water) NSF / ANSI Standard 61 for potable water (CLD 23) AS/NZS 4766 (polyethylene water and chemical tanks) Long term UV stabilization - ASTM 2565 (Cycle 1): Greater than UV-16 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.939 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
ASTM D1693A | ||
10%非离子洗涤剂,模压成型,F50 10% non-ionic detergent, molded, F50 |
200 | hr | ASTM D1693A |
100%非离子洗涤剂,模压成型,F50 100% non-ionic detergent, molded, F50 |
> 1000 | hr | ASTM D1693A |
耐候性 Weathering resistance |
f1 | UL 746C | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ASTM D2240 | ||
拉伸强度 tensile strength 3 |
|||
屈服,3.17 mm,滚塑成型 Yield, 3.17 mm, roll formed 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂,3.17 mm,滚塑成型 Fracture, 3.17 mm, roll formed 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
ASTM D790 | ||
2% 正割,3.17 mm,滚塑成型 2% cut, 3.17 mm, roll formed |
MPa | ASTM D790 | |
正切,3.17 mm,滚塑成型 Tangent, 3.17 mm, roll formed |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ARM冲击 ARM Impact |
|||
-40℃,3.20 mm -40℃,3.20 mm |
J | ||
-40℃,6.35 mm -40℃,6.35 mm |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.17 mm,滚塑成型 1.8 MPa, unannealed, 3.17 mm, roll formed |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm,滚塑成型 0.45 MPa, unannealed, 3.2 mm, roll formed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746A | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
结晶峰温度 Crystallization peak temperature 12 |
|||
DSC DSC 12 |
℃ | ASTM D3418 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 Use conditions B through H per 21 CFR 176.170(c) Table 2. Single use articles containing food types I, II, IV-B, VI-A, VI-B, VII-B, and VIII. Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1. |
2 一般属性:这些不能被视为规格。 |
3 类型 4, 2.0 in/min |
4 0.50 in/min |
5 速率 A (50°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
华北最大地下储气库群再度扩容,库容气量累计超百亿立方米
2021-12-04 搜料网资讯: 11月29日,文13西储气库建成注气,新增库容气量5.69亿立方米,标志着我国华北最大的天然气地下储气库群中原储气库群再度扩容。 这是油田今年建成投运的第2座储气库! |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |