牌号简介 About |
---|
聚苯乙烯945E:是一种超高冲击聚苯乙烯,设计用于需要额外韧性而不牺牲机械性能的应用,具有优异的落镖冲击性能,结合高光泽,使其成为某些ABS应用的候选材料。该聚合物对共挤高光泽片材有较好的效果。945E具有独特的深拉热成型能力,侧壁分布良好。应用:定制板材挤压深拉伸热成型ABS替换超高光泽高冲击应用一般信息:该材料符合21 CFR§177.1640中所述的FDA要求。本材料持有保险商实验室认可94HB;见www.ul.com上的UL文件E55470。USP六级材料安全数据表可帮助客户满足其安全需求。 Polystyrene 945E: Is a super high impact polystyrene designed for applications requiring extra toughness without sacrificing mechanical properties, excellent falling dart impact which, combined with the high gloss, make it a candidate for some ABS applications. This polymer is superior for co-extrusion of high gloss sheet. 945E has unique capabilities for deep draw thermoforming with good sidewall distribution. Application: Custom sheet extrusion Deep draw thermoforming ABS replacement Super high gloss high impact applications General Information: This material complies with FDA requirements as described in 21 CFR §177.1640. This material holds Underwriters Laboratory recognition 94HB; see UL File E55470 at www.UL.com. USP Class VI Material Safety Data Sheets are available to help customers satisfy their safety needs. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
3.5 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 to 0.70 | % | ASTM D955 |
Moisture Moisture |
< 0.10 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2070 | MPa | ASTM D638 |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
热变形温度 Hot deformation temperature |
|||
退火 annealing |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60° 60° |
ASTM D523 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
环保部被取消!其实是“扩权” 塑料工业需留意
2018-03-19 3月13日,国务院机构改革方案公布。根据该方案,改革后,国务院正部级机构减少8个,副部级机构减少7个,除国务院办公厅外,国务院设置组成部门26个。其中,为组建生态环境部,将不再保留环境保护部。 回顾环保部的这些年: 1974年10月,国务院环境保护领导小组正式成立。 1982年5月,国家建委、国家城建总局、建工总局、国家测绘局和国务院环境保护领导小组办公室合并,组建城乡建设环境保护部,部内设环境保护局。 1984年5月,成立国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |