牌号简介 About |
---|
TOPAS 8007F-600是专为与聚乙烯(PE)共混而设计的新型挤出膜级材料。它是一种改进的透明非晶树脂,具有高硬度、防潮性、耐化学性、热成型性和纯度,适用于食品等级和一般用途。它用于铸造和吹制过程中的共混物,以及单层和多层产品。主要的薄膜应用包括扭转包装,形成腹板,保护包装,收缩膜和标签,以及容易撕裂的包装。工业用途包括成型PE和PP板材产品。为了提高性能,在高温下,建议采用更高的玻璃化转变温度(Tg)等级的TOPAS。应用于薄膜保护包装。 TOPAS® 8007F-600 Product Description TOPAS 8007F-600 is a new robust film extrusion grade designed for blending with polyethylene (PE). It is an improved clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Forming films (header bags, etc.) Protective packaging Shrink films and labels Twist films Decorative sheet Food packaging Food contact Leading Attributes Clarity, forming, barrier, purity, halogen-free Stiffness for downgauging, improved forming High shrink, low stress, gloss, toughness Outstanding deadfold, clean cutting Stiffness, chemical resistance, forming, even draw Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 8007F-04 - ultimate clarity extrusion grade TOPAS® 8007F-600 TOPAS® 8007F-600 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Primary characteristic: copolymer. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
1.8 | g/10min | ISO 1133 |
230℃,2.16kg 230℃,2.16kg |
10 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
2.00 | cm³/10min | ISO 1133 |
230℃,2.16 kg 230℃,2.16 kg |
11.0 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸模量 Tensile modulus |
ISO 527-3/1 | ||
MD,70 µm,铸造薄膜 MD, 70 µ m, cast thin film |
MPa | ISO 527-3/1 | |
TD,70 µm,铸造薄膜 TD, 70 µ m, cast thin film |
MPa | ISO 527-3/1 | |
拉伸强度 tensile strength |
ISO 527-3/50 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3/50 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3/50 | |
拉伸应变 Tensile strain |
ISO 527-3/50 | ||
MD,断裂,70 µm,铸造薄膜 MD, fracture, 70 µ m, cast thin film |
% | ISO 527-3/50 | |
TD,断裂,70 µm,铸造薄膜 TD, fracture, 70 µ m, cast thin film |
% | ISO 527-3/50 | |
水气透过率 Water vapor transmittance |
|||
70 µm,23℃,铸造薄膜,85% RH 70 µ m, 23 ℃, cast film, 85% RH |
g·mm/m²/atm/24 hr | ASTM F1249 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,70.0 µm,铸造薄膜 60 °, 70.0 µ m, cast thin film |
ISO 2813 | ||
雾度 Haze |
|||
70.0 µm,铸造薄膜 70.0 µ m, cast thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 90% RH |
3 10°C/min |
【新闻资讯】查看全部
生态环境部就固废与化学品环境管理举行发布会——这些数字很关键
2022-04-08 3月30日,生态环境部举行3月例行新闻发布会,生态环境部固体废物与化学品司司长任勇介绍固体废物与化学品环境管理有关情况并回答记者提问。发布会上出现的几组关键数字,为新污 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |