| 牌号简介 About |
|---|
| Cycoloy C3650树脂阻燃PC/ABS混合物，采用非溴化和非氯化阻燃系统，具有高冲击性和优异的挤出和热成型特性。电缆通道无卤，符合DIN VDE 0472/815 CYCOLOY C3650 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a grade that can be injection molded or extruded into sheet for secondary thermoforming operations. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY C3650 resin is a general purpose resin that is an excellent candidate for a wide variety of applications including cable channels and is verified non-halogen by the DIN VDE 0472/815 standard. |
产品描述 Product Description
用途：电线电缆应用;外壳;
加工条件：型材挤出成型 Profile extrusion
性能特点： 无卤; 防火阻燃等级V-0; 防火阻燃等级5VB; 阻燃; 冲击性能好; High impact resistance,Halogen free,Flame Characteristics,V-0,5VB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
密度 Density |
1.18 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
260℃，5.0kg 260℃，5.0kg |
8.5 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
260℃，5 kg 260℃，5 kg |
8.00 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.40 to 0.60 | % | 内部方法 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ASTM D570 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 9 |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，100 mm跨距 1.8 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Ae | |
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，100 mm跨距 0.45 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Be | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：23~60℃ TD：23~60℃ |
1/℃ | ISO 11359-2 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
MD：23~60℃ MD：23~60℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
IEC 60243-1 | ||
|
0.8 mm，在油中 0.8 mm in oil |
kV/mm | IEC 60243-1 | |
|
1.6 mm，在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
60 Hz 60 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
60 Hz 60 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
2.50 mm 2.50 mm |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/5 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 4 |
% | ASTM D638 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/5 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
|||
|
屈服，50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ISO 2039-2 | ||
|
球压硬度 Ball hardness |
|||
|
H358/30 H358/30 |
MPa | ISO 2039-1 | |
|
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
断裂 fracture |
MPa | ISO 527-2/5 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
屈服 yield |
% | ISO 527-2/5 | |
|
屈服 yield |
% | ISO 527-2/50 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.051 in/min |
| 5 0.079 in/min |
| 6 Yield |
| 7 80*10*4 sp=62mm |
| 8 80*10*4 |
| 9 120*10*4 mm |
| 10 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部
科思创重新任命多个部门主管
2017-08-28 科思创已宣布将在聚氨酯、涂料、粘合剂及其专有化学品部门任用新的部门主管，自2017年9月1日生效。 施乐文博士(Markus Steilemann)将卸任自2016年初开始担任的聚氨酯部门负责人一职，而在明年开始接替帕特里克・托马斯(Patrick Thomas)担任首席执行官。施乐文博士自2017年4月以来一直担任理事会的首席商务官，负责创新、营销和销售。 施乐文博士(Dr. Markus Steilemann)可以回想起在1999年拜耳开始的漫长的国际职 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付