牌号简介 About |
---|
Celanex® 6407是一种30%的玻璃/矿物增强树脂,特别适用于大型外部汽车部件,在这些部件中,延长流动性、平整度和良好的表面外观至关重要。 Celanex 6407 is a 30% glass/mineral reinforced resin particularly suited for large exterior automotive components, where extended flow, flatness and good surface appearance is essential. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.52 | g/cm³ | ASTM D792 |
密度 Density |
1.51 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
12 to 30 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
MD MD |
0.30 to 0.40 | % | ASTM D955 |
TD TD |
0.98 | % | ISO 294-4 |
MD MD |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/1A/5 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
沃特新资料与东芝机械签订临时战略合作意向
2016-04-26 沃特新材料与设备供应商东芝机械株式会社在国际橡塑展第一天签署了长期战略合作意向,将在设备购买、设备研发、行业技术攻关等领域进行战略合作。 据报道,根据协议,200亩的江苏沃特新材料产业园所有挤出生产线将全部优先选用东芝机械的设备。同时,沃特将为东芝提供最前沿的新材料行业动态与需求。此外,双方将强化研发互动交流,希望能够解决一些高分子材料加工方面的行业难点,甚至取得理论上新的突破,为行业整体水平的提升做出贡献。 去年,深圳沃特集团决定建设沃特新材料项目,全套引 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |