牌号简介 About |
---|
Ensinger的Delrin 100AF混合料是一种13%聚四氟乙烯纤维填充的均聚缩醛。与未填充的和聚四氟乙烯粉末填充的缩醛相比,这种先进的缩醛材料具有更好的摩擦系数、更好的润滑性和更好的磨损特性。这种先进的缩醛材料使用均匀分散在Delrin缩醛树脂中的聚四氟乙烯纤维组合。这种结合可以改善磨损特性以及强度、韧性、尺寸稳定性和可加工性。材料的特殊磨损性能和内部润滑有助于减少或消除对外部润滑油的需求。Ensinger还可以生产全强度20%聚四氟乙烯填充版本。Delrin100af通常用于轴承、衬套、凸轮和其他需要额外韧性的减摩装置等应用。优良的磨损特性、自润滑、低摩擦系数、最大未改性韧性、优良的承载特性 Ensinger's DELRIN® 100AF blend stock shapes are a 13% PTFE fiber filled homopolymer acetal. They offer an improved coefficient of friction, better lubricity, and improved wear characteristics over unfilled and PTFE powder filled acetals.This advanced acetal material uses a combination of PTFE fibers uniformly dispersed in Delrin acetal resin. The combination results in improved wear characteristics along with strength, toughness, dimensional stability and machinability. The materials exceptional wear properties and internal lubrication serves to reduce or elimanate the need for external lubricants. Ensinger can also produce a full strength 20% PTFE filled version. DELRIN® 100AF is often used for applications such as bearing, bushings, cams and other antifriction devices that also require extra toughness. Excellent wear characteristics Self lubricating Low coefficient of friction Maximum unmodified toughness Superior load bearing characteristics |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.50 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.12 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
53 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
168 | ℃ | |
1.8 MPa,未退火 1.8 MPa, unannealed |
118 | ℃ | |
熔融温度 Melting temperature |
℃ | ||
使用温度 Operating temperature |
|||
Intermittent Intermittent |
℃ | ||
长期 long-term |
℃ | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
|||
10% 应变,23℃ 10% strain, 23 ℃ |
MPa | ASTM D695 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
2018年双十一中国快递包裹居全球第一
2019-01-09 据国家统计局数据显示,2018年双十一(11月11-16日)业务高峰期间,全国邮政、快递业共处理邮(快)件18.82亿件。中国快递包裹居全球第一,近十年时间增长了二十几倍。在这种高速增长的背后,却是包装耗材的惊人浪费。同时,现时代为了满足消费者任何时候、任何地点、任何方式购买的需求,并提供无差别的购买体验。实体渠道、电商渠道、移动点送、无人零售等多渠道整合的全渠道营销时代已然形成。产品的营销,包装和分销方式正在发生根本性的变化,整个价值链都面临挑战,包装业也必须找到或创造出新的包装解决方案 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |