牌号简介 About |
---|
Tarnoform® 500 GF8玻璃纤维增强注塑等级为40%,具有极高的强度和刚度,收缩率和线性热膨胀系数降低,并且在注塑过程中具有较高的流动性。 Tarnoform® 500 GF8 there is 40% glass fibres reinforced injection-moulding grade with extremely high strength and stiffness and with reduced shrinkage and coefficient of linear thermal expansion, combined with higher flowability during moulding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.71 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
5.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
3.50 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:2.0 mm TD:2.0 mm |
1.1 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
0.50 | % | ISO 294-4 |
吸水率 Water absorption rate |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
Limit of Temperature(a few hours operation) Limit of Temperature(a few hours operation) |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 Hz 1 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 Hz 1 Hz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
UL 94 | ||
燃烧速率 Burning rate |
mm/min | FMVSS 302 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Type ISO Type |
ISO 1874 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 2 |
MPa | ISO 178 | |
弯曲强度 bending strength 2 |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
走出“霾”伏漫漫长途 呼吁塑机行业绿色先行
2017-01-19 这个冬季,我国多个城市遭受雾霾侵袭,PM2.5指数动辄突破400大关,40多个城市相继发布相应级别的重污染天气预警。连日来一直阴魂不散的雾霾,让人们不禁无奈感叹“连呼吸都痛”;更有犀利网友神P图,新增第25节气“立霾”。在搞笑逗趣的段子背后,无法逃避的却是潜伏已久的“恐怖杀手”,正在吞噬着人类的健康。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |