牌号简介 About |
---|
丙烯在复杂的有机金属催化剂作用下聚合得到的产物。它包括长期热稳定性的提高,生产、加工和开发聚丙烯制品时的热氧化降解阻力。用途:双向拉伸,单层和多层金属化膜。技术要求:TU 2211-136-05766801-2006 Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance during PP production, processing and use of PP-made articles. Application: biaxially oriented one- and multi-layer metallized film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | |
表观密度 Apparent density |
0.48 到 0.52 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
1.7 到 2.3 | g/10min | ASTM D1238 |
灰份含量 Ash Content |
0.025 到 0.050 | % | |
凝胶含量 Gel content 2 |
|||
> 200.0 µm > 200.0 µm |
300 | pcs/m² | |
0.700 到 1.50 mm 0.700 to 1.50 mm |
pcs/m² | ||
1.50 到 2.50 mm 1.50 to 2.50 mm |
pcs/m² | ||
> 2.50 mm > 2.50 mm |
pcs/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp 3 |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Thermal Creep Temperature Thermal Creep Temperature 4 |
℃ | ||
热氧化恶化 Thermal oxidation deterioration |
|||
150℃ 150℃ |
day | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
|||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 p.4.8 ?U 2211-136-05766801-2006 |
3 in liquid medium under force 10 H |
4 at load 0.46 H/mm² |
【新闻资讯】查看全部
新车难提 二手车涨价 全球汽车芯片短缺波及车市
2021-09-26 搜料网资讯: 俗话说金九银十购车季,在全球汽车芯片短缺的情况下,今年的金九银十的车市有了哪些新变化?中秋小长假期间,北京青年报记者走访多家汽车4S店和二手车交易市场发 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |