BC545MO是一种低脸红聚丙烯异相共聚物,用于注塑成型。该牌号具有高冲击强度、高热稳定性和良好的加工性能。与所有聚丙烯一样,该等级的聚丙烯具有优异的应力开裂和耐化学性。这一等级的特点是结合了高硬度,非常高的冲击强度和低应力美白。这一等级是温和的核化,以最大限度地提高刚度冲击平衡。添加剂配方提供长期的热稳定性。它非常好的感官性能使这种等级可以用于任何母粒,而不会变色问题。 BC545MO is a low-blush polypropylene heterophasic copolymer. This grade features high impact strength, high thermal stability and very good processability. As all polypropylenes, this grade shows excellent stress-cracking and chemical resistances. This grade is characterized by combination of high stiffness, very high impact strength, low stress whitening and good electrical properties. This grade is mildly nucleated to maximize the stiffness-impact balance. The additive formulation provides long-term heat stability. Its very good organoleptic properties allows this grade to be used with any masterbatch without discoloring problems. Applications Suitcases Technical parts Battery cases Communication cables (UL 444) Crates and boxes Special Features Good processability High stiffness Good melt stability High impact strength Very good stress crack resistance Good conductor adhesion Very good chemical resistance Dielectric properties |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.908 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
3.5 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
1.5 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
1250 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
25.0 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
注塑成型 injection molding 2 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-1A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 3 |
|||
1.8 MPa,未退火 1.8 MPa, unannealed 3 |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed 3 |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A | |
-- -- |
℃ | ISO 306/B | |
Melt Energy Melt Energy |
kJ/kg | ISO 11357 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 Injection molded |
【新闻资讯】查看全部
陶氏化学完成出售MEGlobal公司局部股权的买卖
2015-12-31 陶氏化学12月24日宣布,公司已经完成向伊奎特石化公司出售MEGlobal公司部分股权的交易,并收到了15亿美元的税前款项。 陶氏化学此前宣布打算优化在科威特合资企业中的所有权,该交易的完成代表这一行动取得了进展。MEGlobal是全球领先的乙二醇单体和二甘醇生产商和销售商,总部位于迪拜,创建于2004年7月,当前年产250万吨二甘醇。 MEGlobal是陶氏化学和科威特石化工业公司的合资企业。向伊奎特石化公司出售部分股权后,陶氏化学仍然持有MEGlobal |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |