牌号简介 About |
---|
Sarlink ML-1100是一个通用热塑性弹性体系列,可用于NAT和BLK,设计用于汽车内部应用。Sarlink ML-1180N NaT是一种中等硬度、高密度、填充等级的注塑成型材料。 Sarlink ML-1100 is a general purpose thermoplastic elastomer series, available in NAT and BLK designed for automotive interior applications. Sarlink ML-1180N NAT is a medium hardness, high density, filled grade suitable for injection molding. |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ISO 37 | ||
断裂 fracture |
6.40 | MPa | ISO 37 |
MD,断裂 MD, fracture |
6.30 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
ISO 37 | ||
断裂 fracture |
730 | % | ISO 37 |
流量,断裂 Flow rate, fracture |
630 | % | ISO 37 |
撕裂强度 tear strength 3 |
ISO 34-1 | ||
TD TD |
31 | kN/m | ISO 34-1 |
MD MD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 4 |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
90℃,70 hr 90℃,70 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,1 秒,注塑成型 Shore A, 1 second, injection molding |
ISO 868 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ISO 868 | ||
邵氏 A,15 秒,注塑成型 Shore A, 15 seconds, injection molding |
ISO 868 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ISO 188 | |
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
MD:125℃,168 hr MD:125℃,168 hr |
% | ISO 188 | |
TD:100% 应变 125℃,168 hr TD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
流量:110℃,1008 hr Flow rate: 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
流量:125℃,168 hr Flow rate: 125 ℃, 168 hr |
% | ISO 188 | |
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 6 |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 7 |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 8 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 6 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 7 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 8 |
ISO 188 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 | |
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TD,100% 应变 TD, 100% strain |
MPa | ISO 37 | |
MD,100% 应变 MD, 100% strain |
MPa | ISO 37 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 20 in/min |
3 B 方法,直角形试样(不割口), 20 in/min |
4 类型 A |
5 类型 1 |
6 1 sec |
7 5 sec |
8 15 sec |
【新闻资讯】查看全部
德国两大石油公司估计近期将签署兼并协议
2018-03-07 3月4日奥斯陆报道,德国莱茵集团(RWE)麾下的石油子公司DEA的首席执行官M・M・汉森周四在奥斯陆披露,DEA和德国化工巨头巴斯夫旗下的石油子公司温特斯豪(Wintershall)将很有可能在3月或4月签署一项旨在合并两家石油公司的最终协议。 汉森是在奥斯陆举行的一次会议上对与会者发表上述讲话的。她说,两家公司打算在今年年底前完成这笔交易并计划在交易完成以后的18个月里上市新公司。 巴斯夫公司说,这笔交易将可能在今年第三季度结束前完成。 汉 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-Sarlink® TPE ML-1180N NAT (PRELIMINARY DATA)证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)