| 牌号简介 About |
|---|
| LE6022是一种黑色低密度共聚物改性聚乙烯化合物。具有优异的抗应力开裂性能和力学性能，低温性能和良好的挤出性。LE6022含有2.5%分散性良好的funace黑色，以确保优异的耐候性。应用LE6022设计用于通信电缆的护套。采用声音挤压实践生产的LE6022电缆通常符合以下电缆产品标准：IEC 60502，第2部分，ST3型，IEC 60708，IEC 60840，ST3型，HD 620 S2，第1部分，表4B，DMP 17 LE6022 is a black low density copolymer modified polyethylene compound. It is characterized by excellent stress crack resistance and mechanical properties and low temperature performance in combination with good extrudability. LE6022 contains 2,5% well dispersed furnace black in order to ensure excellent weathering resistance. Applications LE6022 is designed for jacketing of communication cables. Specifications LE6022 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure: ASTM D 1248 Type I, Class C, Category 5, Grade E5, J3, W2-4 ISO 1872-PE, KCHL, 18-D003 The following cable material standards are met by LE6022: EN 50290-2-24 DIN VDE 0207 Type 2YM2 Cables manufactured with LE6022 using sound extrusion practice normally comply with the following cable product standards: IEC 60502, Part 2, Type ST3 IEC 60708 IEC 60840, Type ST3 HD 620 S2, Part 1, table 4B, DMP 17 |
产品描述 Product Description
用途：电缆护套;
加工条件：挤出 Extrusion
性能特点： 共聚物; 表面光泽度好; 低密度; 抗应力开裂; 耐候抗UV; Weather resistance is good,Good surface appearance,Low density,Copolymer,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
ISO 1183 | ||
|
-- -- 2 |
0.931 | g/cm³ | ISO 1183 |
|
-- -- 3 |
0.918 | g/cm³ | ISO 1183 |
|
表观密度 Apparent density |
0.50 to 0.60 | g/cm³ | |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.20 | g/10min | ISO 1133 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
50 ℃，10%非离子表面活性剂，F20 50 ℃, 10% non-ionic surfactant, F20 |
> 1000 | hr | IEC 60811-4-1 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，1 秒 Shore D, 1 second |
ISO 868 | ||
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Compound |
| 3 Base Resin |
|
【新闻资讯】查看全部 
美国墨西哥湾现货聚合级丙烯价格创历史新高
2021-02-20 搜料网资讯： 2月19日，因整个地区冬季极端天气导致的供应紧张和装置下线，美国墨西哥湾沿岸聚合物级丙烯现货价格创下历史新高。 标普全球普氏公司2月19日评估聚合级丙烯现货价格 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付