聚丙烯用于制造薄膜、胶带、香烟和糖果包装纸、化妆品、医药和食品包装材料。高清晰度。热灌装应用。活铰链。聚乙烯无规共聚物PP广泛应用于以下领域:注射成型:家庭用品、午餐盒和铅笔盒“活铰链”吹塑成型:婴儿奶瓶、果汁瓶、茶、水、药品和化妆品经济性好。热灌装应用。极好的胶片清晰度。韧性好。乙烯均聚物PP是一系列应用的首选材料:胶带挤出:大米、水泥和工业化学品用编织袋薄膜:胶带用双向、铸造和充气薄膜、包装和标签注射成型:整体家具、提桶、家庭用品、容器、玩具、帽热成型:快餐容器,矿泉水杯 EVALENE ® PHF1001 is designed for iPP in the 15 to 100 microns (0.0006" to 0.004") thickness range. Outstanding clarity and gloss, ease of opening and superior toughness are key properties of EVALENE ® PHF1001 films. These films have inherent clarity that translates to stunning packaging for maximum consumer appeal. They likewise have superior toughness that assures packaging integrity and protection. FEATURES Outstanding optical properties Excellent openability Superior toughness Good organoleptic properties Meets FDA Philippines food-contact requirements Halal certified TYPICAL APPLICATIONS Films from 15 to 100 microns (0.0006" to 0.004") for food and garment packaging |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
10 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
动态 dynamic |
0.15 | ASTM D1894 | |
静态 static state |
0.26 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
30 | µm | |
割线模量 Secant modulus 2 |
ASTM D882 | ||
1% 正割,MD:30 µm 1% secant, MD: 30 µ m |
711 | MPa | ASTM D882 |
1% 正割,TD:30 µm 1% secant, TD: 30 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength 3 |
ASTM D882 | ||
MD,屈服,30 µm MD, yield, 30 µ m |
MPa | ASTM D882 | |
TD,屈服,30 µm TD, yield, 30 µ m |
MPa | ASTM D882 | |
MD,断裂,30 µm MD, fracture, 30 µ m |
MPa | ASTM D882 | |
TD,断裂,30 µm TD, fracture, 30 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,屈服,30 µm MD, yield, 30 µ m |
% | ASTM D882 | |
TD,屈服,30 µm TD, yield, 30 µ m |
% | ASTM D882 | |
MD,断裂,30 µm MD, fracture, 30 µ m |
% | ASTM D882 | |
TD,断裂,30 µm TD, fracture, 30 µ m |
% | ASTM D882 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:30 µm MD:30 µm |
g | ASTM D1922 | |
TD:30 µm TD:30 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,30.0 µm 60°,30.0 µm |
ASTM D2457 | ||
雾度 Haze |
|||
30 µm 30 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 2.0 in/min |
4 0.051 in/min |
5 10°C/min, 2nd heating |
【新闻资讯】查看全部
提早开发将成为塑料模具行业开展新趋势
2016-10-19 目前,电视机和显示器外壳、空调器外壳、摩托车塑件等已采用提前开发这种方法,即大力提高开发能力,将开发工作尽量往前推,直至介入到模具用户的产品开发中去,甚至在尚无明确用户对象之前进行开发,变被动为主动。此外,手机和电话机模具开发也已开始尝试。这种做法打破了长期以来,模具厂只能等有了合同,才能根据用户要求进行模具设计的被动局面。 随着模具企业设计和加工水平的提高,模具的制造正在从过去主要依靠钳工的技艺转变为主要依靠技术。这不仅是生产手段的转变,也是生产方式的转变和观念的上升。这 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |