| 牌号简介 About |
|---|
| Ultramid® B3WM8 (8260 HS) BK00102是一种热稳定，色素黑色，40%矿物增强PA6注射成型树脂。它具有较高的刚度、尺寸稳定性和耐热性，同时具有良好的加工性能，包括低翘曲性和抗沉痕形成性。它对油脂、油和碳氢化合物具有固有的耐化学性。应用Ultramid® B3WM8 (8260 HS) BK00102通常推荐用于船用五金件、支架、配件、线轴、办公家具、电器组件和电动工具外壳等应用。 Ultramid B3WM8 BK00102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It maintains its inherent chemical resistance to greases, oils and hydrocarbons. Applications Ultramid B3WM8 BK00102 is generally recommended for applications such as marine hardware, brackets, fittings, bobbins, office furniture, appliance components, and power tool housings. |
产品描述 Product Description
用途：家电部件;线轴;家具;船舶应用;配件;外壳;
颜色：黑色
加工条件：注射成型 Injection Molding
性能特点： 热稳定性好; 机械强度好; 耐油; 尺寸稳定性好; 耐碳氢化合物; 耐高温; 低翘曲性; 易加工; Good Rigidity,Low warping,Excellent Processability,Good Dimensional Stability,High Heat Resistance,Grease resistance,Heat Stabilized,Hydrocarbons
填料：矿物 40
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.49 | g/cm³ | ASTM D792 |
|
密度 Density |
1.49 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.90 | % | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
5.7 | % | ISO 62 |
|
饱和 saturated |
5.7 | % | ASTM D570 |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
平衡，50% RH Balance, 50% RH |
% | ASTM D570 | |
|
24hr 24hr |
% | ASTM D570 | |
|
23℃，24hr 23℃，24hr |
% | ISO 62 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ASTM E831 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
ISO 527-2 | ||
|
-40℃ -40℃ |
MPa | ISO 527-2 | |
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
80℃ 80℃ |
MPa | ISO 527-2 | |
|
120℃ 120℃ |
MPa | ISO 527-2 | |
|
150℃ 150℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
断裂，-40℃ Fracture, -40 ℃ |
MPa | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
断裂，80℃ Fracture, 80 ℃ |
MPa | ASTM D638 | |
|
断裂，121℃ Fracture, 121 ℃ |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
断裂，-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
断裂，80℃ Fracture, 80 ℃ |
MPa | ISO 527-2 | |
|
断裂，120℃ Fracture, 120 ℃ |
MPa | ISO 527-2 | |
|
断裂，150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
ASTM D638 | ||
|
断裂，-40℃ Fracture, -40 ℃ |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂，80℃ Fracture, 80 ℃ |
% | ASTM D638 | |
|
断裂，121℃ Fracture, 121 ℃ |
% | ASTM D638 | |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
断裂，-40℃ Fracture, -40 ℃ |
% | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
断裂，80℃ Fracture, 80 ℃ |
% | ISO 527-2 | |
|
断裂，120℃ Fracture, 120 ℃ |
% | ISO 527-2 | |
|
断裂，150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
快递包装渣滓成隐患 专家呼吁成立回收体系
2016-04-07 大陆网购发达，快递业迅速成长，大量累积的垃圾也成为问题。据悉，北京一家卖母婴产品的网店为了获得买家“包装严密”的好评，每个月使用近2万米的胶带包装。快递包装产生的大量垃圾引起注意，专家呼吁成立回收体系。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付