牌号简介 About |
---|
KetaSpire KT- 820 SL45是基于聚醚醚酮的树脂,专门设计用于需要极低磨损率和良好机械性能的需要使用外部润滑剂的产品。 KetaSpire® KT-820 SL45 is a PEEK based compound specifically designed to provide exceptionally low wear rates and good mechanical properties in applications where an external lubricant is provided. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
69 | J/m | ASTM D256 |
-- -- |
8.5 | kJ/m² | ISO 180 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-- -- |
530 | J/m | ASTM D4812 |
-- -- |
43 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
299 | ℃ | ASTM D648 |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
DSC | ||
50℃ 50℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/5 | |
-- -- |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/1A/5 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
摩擦系数 friction coefficient |
|||
-- -- 4 |
ASTM D1894 | ||
-- -- 5 |
ASTM D3702 | ||
-- -- 6 |
ASTM D1894 | ||
-- -- 7 |
ASTM D3702 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,2.16kg 400℃,2.16kg |
g/10min | ASTM D1238 | |
收缩率 Shrinkage rate 2 |
ASTM D955 | ||
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt 2 |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 2 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5" x 0.5" x 0.125" bars |
3 0.20 in/min |
4 润滑条件: 75 fpm, 1000 psi (0.38 m/s , 6895 kPa) |
5 润滑条件: 800 fpm , 750 psi (6.06 m/s , 5171 kPa) |
6 干燥条件: 800 fpm ,31.25 psi (4.06 m/s , 215 kPa). |
7 干燥条件: 200 fpm ,125 psi (1.02 m/s , 862 kPa). 不推荐 50 fpm ,500 psi (0.25 m/s , 3447 kPa). |
【新闻资讯】查看全部
巴斯夫、陶氏、三桶油、万华、恒力……34家化企业绩一览!
2022-05-07 国外 巴斯夫 (BASF) 2021年销售额达到786亿欧元(约826亿美元),比2020年提升33%,不计特殊项目的息税前收益为78亿欧元(同比增长118%),达到2020年的两倍多,相比2019年疫情前水平则 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |