| 牌号简介 About |
|---|
| 基于PA 10T VESTAMID® HTplus M3000 NC的聚邻苯二甲酰胺是一种基于PA 10T的天然有色共聚酰胺。PA 10T是1，10-十亚甲基二胺（10）和对苯二甲酸（T）的缩聚产物。由于1,10-十亚甲基二胺是从蓖麻油中提取的，因此VESTAMID® HTplus M3000 NC是部分天然资源，因此是基于生物的。与基于PA 6T的树脂相比，VESTAMID® HTplus M3000 NC具有更宽的加工窗口和更低的吸水倾向。因此，材料的力学性能和尺寸随湿度的变化较小。该树脂特别适用于制造高温零件。 Polyphthalamide based on PA 10T VESTAMID HTplus M3000 nc is a natural colored PA 10T-based copolyamide. PA 10T is a polycondensation product of 1,10-decamethylene diamine (10) and terephthalic acid (T). As 1,10-decamethylene diamine is derived from castor oil, VESTAMID HTplus M3000 nc is partially natural resourced and thus bio-based. Compared to PA 6T-based resins VESTAMID HTplus M3000 nc has a broader processing window as well as a reduced tendency to absorb water. Therefore the material exhibits less variation in mechanical properties and dimensional changes with humidity. The resin is especially suited for manufacturing parts subjected to high temperature. |
产品描述 Product Description
用途：高温应用;
性能特点： 可回收; 共聚物; 耐高温; Renewable resources,High Heat Resistance,Copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.10 | g/cm³ | ISO 1183 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
2700 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
73.0 | MPa | ISO 527-2 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
5.0 | % | ISO 527-2 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
-40℃，完全断裂 -40 ℃, completely fractured |
5.5 | kJ/m² | |
|
23℃，完全断裂 23 ℃, completely fractured |
kJ/m² | ||
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
-40℃，完全断裂 -40 ℃, completely fractured |
kJ/m² | ||
|
23℃，完全断裂 23 ℃, completely fractured |
kJ/m² | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
| 备注 |
|---|
| 2、2nd heating |
|
【新闻资讯】查看全部 
科思创感光薄膜助推汽车透明显示应用发展
2021-02-03 搜料网资讯： 苏格兰技术提供商Ceres Holographics宣布与科思创建立战略合作伙伴关系，将BayfolHX感光聚合物薄膜商业化，用于汽车透明显示应用。Ceres Holographics利用这些薄膜创建具有定制 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付