牌号简介 About |
---|
POM共聚物产品,具有低排放特性,尤其适用于汽车内饰。高硬度、硬度和韧性等标准注射成型等级的良好性能;对溶剂、燃料和强碱具有良好的耐化学性,以及良好的抗水解性;根据VDA 275<10 mg/kg(天然等级)单体和添加剂,保持了高耐热性和氧化降解性。根据21 CFR 177.2470燃烧率ISO 3795和厚度大于1 mm的FMVSS 302<75 mm/min,在符合欧盟法规(EU)10/2011 FDA的要求中列出。FDA=食品药品监督管理局(美国)fmvss=联邦机动车辆安全标准(美国) POM copolymer Product with reduced emissions especially for automotive interior application. Good properties of the standard-injection molding grades like high rigidity, hardness and toughness; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation are maintained Emission according to VDA 275 <10 mg/kg (natural grades) Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm. FDA = Food and Drug Administration (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA) |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2850 | MPa | ISO 527-2/1A/1 |
拉伸强度 tensile strength |
|||
屈服 yield |
64.0 | MPa | ISO 527-2/1A/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
9.0 | % | ISO 527-2/1A/50 |
标称拉伸断裂应变 Nominal tensile fracture strain |
30 | % | ISO 527-2/1A/50 |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
2500 | MPa | ISO 899-1 |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 | |
Effective Thermal Diffusivity Effective Thermal Diffusivity |
m²/s | Internal Method | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
熔体密度 Melt density |
g/cm³ | Internal Method | |
Melt Specific Heat Melt Specific Heat |
J/kg/℃ | Internal Method | |
熔体导热性 Melt thermal conductivity |
W/m/K | Internal Method | |
顶出温度 Ejection temperature |
℃ | Internal Method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
索尔维代表比利时参加迪拜世博会
2021-10-24 搜料网资讯: 布鲁塞尔,2021年9月29日索尔维自豪地宣布将参加2021年10月1日开幕的2021-2022迪拜世界博览会,并有幸成为比利时国家馆的重要组成部分。届时来自布鲁塞尔、佛兰德斯和瓦 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |