牌号简介 About |
---|
洛特利24MA02是由乙烯和丙烯酸甲酯经高压自由基聚合而成的无规共聚物。由于丙烯酸甲酯含量的原因,在需要柔软性、柔韧性和极性的应用中可以使用乐泰24MA02。典型应用是柔性薄膜、聚酯改性和电缆化合物。 LOTRYL® 24MA02 is a random copolymer of Ethylene and Methyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to its high methyl acrylate content, LOTRYL® 24MA02 can be used for applications where softness, flexibility and polarity are required. Typical applications are flexible film, polyesters modification, masterbatch carrier resin and cable compounds. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 to 3.0 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
1.0 to 3.0 | g/10min | ISO 1133 |
甲基丙烯酸含量 Methacrylic acid content |
23.0 to 26.0 | wt% | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,模压成型 Shaw A, molded |
ISO 868 | ||
邵氏 A,模压成型 Shaw A, molded |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2 | |
断裂,模压成型 Fracture, molded |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ISO 527-2 | |
断裂,模压成型 Fracture, molded |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
模压成型 Compression Molding |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
99%灭活!SUKANO生产高性能抗病毒色母粒
2021-02-20 搜料网资讯: 如今,新冠病毒大流行提高了人们对全世界卫生与健康的认识。尽管接触表面对于传播病毒方面影响不大,但人们对其卫生需求在不断增加, 主要体现在包装、纺织品、工 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |